- Polykemi AB POLYelast TPE HJ-75 UV Thermoplastic Elastomer, PP/Elastomer/Mineral, UV-Stabilized, Low CLTE
Polykemi AB POLYelast TPE HJ-75 UV Thermoplastic Elastomer, PP/Elastomer/Mineral, UV-Stabilized, Low CLTE
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE HJ-75 UV Thermoplastic Elastomer, PP/Elastomer/Mineral, UV-Stabilized, Low CLTE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | ISO 1183 |
| Filler Content | 12 % | 12 % | ±2%; Polykemi |
| Melt Index of Compound | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 @Time 15.0 sec |
55 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 18.0 MPa | <= 2610 psi | ISO/R527 |
| Elongation at Break | >= 100 % | >= 100 % | ISO/R527 |
| Flexural Modulus | 1.00 GPa @Temperature 23.0 °C |
145 ksi @Temperature 73.4 °F |
ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180/4A |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -20.0 °C |
3.81 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 65.0 µm/m-°C | 36.1 µin/in-°F | Polykemi |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 125 °C @Load 1.00 kg |
257 °F @Load 2.21 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Injection Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Hexcel® HexWeb® HRH-36/OX - 3/16 - 2.0 Para-Aramid/Phenolic Core
- A. Schulman POLYBATCH™ Ivory 90033/4 Concentrate Based In LDPE
- ChevronTexaco Delo® 477 CFO Marine Engine Oil, SAE 40
- Epoxy Technology EPO-TEK® U300-2 Two Component Epoxy
- BYK Cloisite® 20A Nanoclay
- Cast Nylons Nycast® 6PA-MoS2 Nylon 6
- Akzo Nobel Trigonox® KSM Peroxide Cure Agent
- Aremco Ceramacast™ 895 High Temperature Potting & Casting Material Alumina
- 3M 7011 Performance Paper Label Material
Copyright © lookpolymers.com All Rights Reserved