- SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66
SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RB006 is a compound based on Nylon 66 resin containing 30% Glass Bead.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.720 % | 0.720 % | 50% RH, 24 hrs; ASTM D570 |
| 0.720 % | 0.720 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D638 | |
| 66.0 MPa | 9570 psi | ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| 6.5 % | 6.5 % | Type I, 5 mm/min; ASTM D638 | |
| 7.6 % | 7.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.81 GPa | 988 ksi | 50 mm/min; ASTM D638 |
| 7.28 GPa | 1060 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 87.0 MPa | 12600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 124 MPa | 18000 psi | ASTM D790 | |
| Flexural Modulus | 3.84 GPa | 557 ksi | 2 mm/min; ISO 178 |
| 4.05 GPa | 587 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 4.69 GPa | 680 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.90 J/cm | 7.31 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 62.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 61.9 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs PB300 PbCO3 Lead(II) carbonate
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR N330 (HAF) Filler
- DSM Akulon® K224-TG9/A Nylon 6-45% Glass Reinforced (European Grade) (Dry) (discontinued **)
- Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Annealed Tube
- A. Schulman PAPERMATCH® H-5338 Specialty Masterbatch
- Abatron AboCast 8110-1/AboCure 8110-3 Flexible Epoxy
- 3M QSLV-M-2-500 Cold Shrink Quick Splice Low Voltage
- Ashley Polymers Ashlene® 833 Nylon 6
- BASF Capron® GR20 HS 20% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- Elisto THERMOSTAR® MD 100 Pattern material
Copyright © lookpolymers.com All Rights Reserved