- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 417 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 417 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1, -2 |
| Lanxess Durethan® A 30 S H3.0 000000 Nylon 66, Injection Molding PA 66, non-reinforced, injection moldingInformation provided by LANXESS. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP IFP36 PA6.12 LNP* LUBRICOMP* IFP36 is a Nylon 6/12 base resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of t his grade include: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp JL003 PES LNP* Lubricomp* JL003 is a compound based on Polyethersulfone resin containing PTFE.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP JZL012 PES (Europe-Africa-Middle East) LNP* LUBRICOMP* JZL012 is a compound based on Polyethersulfone resin containing Proprietary Filler, PTFE. Added features include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM DH1004 PEI |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM DH1004 PEI (Asia Pacific) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM DH1004 PEI (Europe-Africa-Middle East) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. RoHS compliant and UL94 V0 listed. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem DH1004F PEI High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Americas regi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON PFD04 PA 6 LNP* STAT-KON* PFD04 is a compound based on Nylon 6 containing 20% Glass Fiber. Added feature of this grade is: Ellectrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON PFD04S PA 6 (Europe-Africa-Middle East) LNP* Statkon* PFD04S is a compound based on PA 6 resin containing Glass Fiber, Carbon Powder. Added features include: Electrically Conductive, Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON PX93058 PA 6 (Europe-Africa-Middle East) LNP*STATKON*PX93058 is a compound based on PA 6 resin containing Carbon Powder, Glass Fiber. Added features include: Electrically Conductive, Easy Molding, Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP EF006 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* EF006 is a compound based on Polyetherimide resin containing Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP JF003XXZ PES LNP* THERMOCOMP* JF003XXZ is a compound based on Polyethersulfone resin containing 15% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOTUF IX02582 PA6.12 LNP* Thermotuf* IX02582 is a compound based on Nylon 6/12 resin containing Proprietary Filler(s). Added features of this material include: High Impact. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 9090 PEI Polyetherimide Blend with improved Ductility and Detergent resistance. Meets FAR 25.853 and OSU 55/55 heat release and provides low toxicity, smoke and flame evolution. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 9090 PEI (Europe-Africa-Middle East) Polyetherimide Blend with improved Ductility and Detergent resistance. Meets FAR 25.853 and OSU 55/55 heat release and provides low toxicity, smoke and flame evolution. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP 9X10401H ABS LNP* THERMOCOMP* 9X10401H is a compound based on Polyphenylsulfone containing proprietary filler(s). Added feature of this grade is: X-Ray Opaque. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOTUF PX95726 PA 6 LNP THERMOTUF* PX95726 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® VB-5150GL PBT, 15% Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1/-2 |
| Unitika A1022GFL15 PA6, 15% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
| Westlake Plastics Polyethersulfone High resistance to heat and combustibility, low smoke emission, and transparency are the combination of properties possessed by stock shapes extruded from PES. These, coupled with light weight, good.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
| Westlake Plastics Radel® R 5500 Polyphenylsulfone Stock shapes extruded from Radel R resins offer a superior combination of high performance properties that include excellent thermal stability, outstanding toughness, and good environmental stress c.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
| Westlake Plastics Radel® R 5500 Polyphenylsulfone For Medical Applications Medical grade Radel R5500 resin offers exceptional hydrolytic stability, toughness, heat deflection temperature and resistance to stress cracking. This polymer also has excellent thermal stability,.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
| A. Schulman ComAlloy Comtuf® 613 Nylon 6, Glass Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1/-2 |
| BASF Ultramid® B35G3 BK 00564 15% Glass Filled PA6 (Dry) Description: 15% glass fiber reinforced injection molding grade e.g. for internal gas pressure applications such as flashing direction switch gears, automobile mirror housings and wheels of mountain.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP VERTON PX00700 PA 6 (Asia Pacific) LNP* Verton* PX00700 is a compound based on Nylon 6 resin containing Long Glass Fiber. |
|||