SABIC Innovative Plastics LNP THERMOCOMP JF003XXZ PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP JF003XXZ PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* JF003XXZ is a compound based on Polyethersulfone resin containing 15% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.300 % | 0.300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0051 cm/cm @Time 86400 sec |
0.0051 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0067 cm/cm @Time 86400 sec |
0.0067 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 109 MPa | 15800 psi | ASTM D638 |
| 110 MPa | 16000 psi | ISO 527 | |
| Tensile Strength, Yield | 109 MPa | 15800 psi | ASTM D638 |
| 110 MPa | 16000 psi | ISO 527 | |
| Elongation at Break | 3.1 % | 3.1 % | ISO 527 |
| 3.2 % | 3.2 % | ASTM D638 | |
| Elongation at Yield | 3.1 % | 3.1 % | ISO 527 |
| 3.2 % | 3.2 % | ASTM D638 | |
| Tensile Modulus | 6.20 GPa | 899 ksi | 50 mm/min; ASTM D638 |
| 6.41 GPa | 930 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| 176 MPa | 25500 psi | ISO 178 | |
| Flexural Modulus | 5.50 GPa | 798 ksi | ISO 178 |
| 5.51 GPa | 799 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.67 J/cm | 12.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 47.0 kJ/m² | 22.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 5.40 µm/m-°C @Temperature -40.0 - 40.0 °C |
3.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 55.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 3.60 µm/m-°C @Temperature -40.0 - 40.0 °C |
2.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 28.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Network Polymers NPP 25-1010
- Teknor Apex APEX® 90-A41R-65-NT Polyvinyl Chloride, Flexible
- Lubrizol Estane® S360D Thermoplastic Polyurethane
- Unitika elitel UE3250 Polyester, Pellet
- C.O.I.M. EXTER S® S 108 A Orthophthalic Resin
- Carpenter Super Invar 32-5
- 3M Scotchcal™ 50-49 Graphic Film
- Solvay Specialty Polymers Hylar® MP20 PVDF Polyvinylidene Fluoride (discontinued **)
- Ashley Polymers Ashlene® 524 Nylon 66
Copyright © lookpolymers.com All Rights Reserved