- Unitika A1022GFL15 PA6, 15% Glass Fiber Reinforced, Dry
Unitika A1022GFL15 PA6, 15% Glass Fiber Reinforced, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1022GFL15 PA6, 15% Glass Fiber Reinforced, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 % @Time 86400 sec |
1.5 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ISO 2039 |
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527-1/-2 |
| Tensile Modulus | 5.60 GPa | 812 ksi | ISO 527-1/-2 |
| Flexural Strength | 175 MPa | 25400 psi | ISO 178 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.30 J/cm² | 10.9 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 42.0 µm/m-°C | 23.3 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.860 mm |
HB @Thickness 0.0339 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 39.0 kV/mm @Thickness 1.00 mm |
991 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
Users viewing this material also viewed the following:
- MV Labs AG165 KAg(CN)2 Potassium dicyanoargentate(I)
- Precision Polymer Engineering Z75L Hydrogenated NBR Compound
- SABIC Innovative Plastics Cycoloy® C2800 PC+ABS (Asia Pacific)
- Materion BrushCAST® 275CT Fine Grain Casting Alloy (Solution Annealed & Aged)
- DuPont Nucrel® 403 Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film
- ChevronTexaco Transultex® CF G
- 3M OFM0109 Outdoor UL Recognized Polyester Overlaminate Label Products
- 3M Scotchcal™ 1000-27 Graphic Film
- Gromax CCP PBT 5630-200C 30% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved