SABIC Innovative Plastics ULTEM 9090 PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 9090 PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyetherimide Blend with improved Ductility and Detergent resistance. Meets FAR 25.853 and OSU 55/55 heat release and provides low toxicity, smoke and flame evolution.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10 g/10 min @Load 6.60 kg, Temperature 337 °C |
10 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 14 g/10 min @Load 5.00 kg, Temperature 360 °C |
14 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
| 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
| 97.0 MPa | 14100 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 80 % | 80 % | 50 mm/min; ISO 527 |
| 85 % | 85 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 |
| 7.0 % | 7.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.90 GPa | 421 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 136 MPa | 19700 psi | 2 mm/min; ISO 178 |
| 140 MPa | 20300 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.80 GPa | 406 ksi | 2 mm/min; ISO 178 |
| 3.00 GPa | 435 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| 33.0 J/cm @Thickness 3.20 mm |
61.8 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/2C |
| Dart Drop, Total Energy | 88.0 J @Temperature 23.0 °C |
64.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| 88.0 J @Temperature -20.0 °C |
64.9 ft-lb @Temperature -4.00 °F |
ASTM D3763 | |
| 99.0 J @Temperature 0.000 °C |
73.0 ft-lb @Temperature 32.0 °F |
ASTM D3763 | |
| Impact | 90 @Temperature -20.0 °C |
90 @Temperature -4.00 °F |
Instrumented Impact Ductility, %; ASTM D3763 |
| 100 @Temperature 23.0 °C |
100 @Temperature 73.4 °F |
Instrumented Impact Ductility, %; ASTM D3763 | |
| 100 @Temperature 0.000 °C |
100 @Temperature 32.0 °F |
Instrumented Impact Ductility, %; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 56.0 µm/m-°C @Temperature -20.0 - 150 °C |
31.1 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 55.0 µm/m-°C @Temperature -20.0 - 150 °C |
30.6 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 212 °C | 414 °F | Rate B/50; ISO 306 |
| 212 °C | 414 °F | Rate B/120; ISO 306 | |
| 219 °C | 426 °F | Rate A/50; ISO 306 | |
| Oxygen Index | 46 % | 46 % | ASTM D2863 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| NBS Smoke Density, Flaming, Ds 4 min | 0.7 | ASTM E 662 |
| OSU total heat release (2 minute test) | 15kW-min/m^2 | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 45kW/m^2 | FAR 25.853 |
| Vertical Burn a (60s) passes at | 1sec | FAR 25.853 |
Users viewing this material also viewed the following:
- OCTAL DPET™/PE Laminate Sheet with Improved Barrier Properties
- Permabond ES578 Epoxy Resin
- LATI Latigloss 66 H2 K/30 PA 66, 30% Carbon Fiber Reinforced, Heat Stabilized
- Haynes 718 alloy, cold rolled, solution-treated and aged sheet
- Stir SpA SPI 65 (PVC)
- SABIC Innovative Plastics Noryl HS2000 PPE (Asia Pacific)
- Solvay TOLCIDE® PS 75LT 75% tetrakis hydroxymethyl phosphonium sulfate
- A. Schulman POLYBATCH™ Navajo 10275U/4 Concentrate Based In LDPE
- A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin
Copyright © lookpolymers.com All Rights Reserved