SABIC Innovative Plastics LNP LUBRICOMP JZL012 PES (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP JZL012 PES (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* JZL012 is a compound based on Polyethersulfone resin containing Proprietary Filler, PTFE. Added features include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 75.0 MPa
10900 psi
5 mm/min; ISO 527
Elongation at Break 5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 3.00 GPa
435 ksi
1 mm/min; ISO 527
Flexural Yield Strength 106 MPa
15400 psi
2 mm/min; ISO 178
Flexural Modulus 3.10 GPa
450 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 214 °C
417 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 199 °C
390 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af