SABIC Innovative Plastics LNP STAT-KON PFD04 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON PFD04 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* PFD04 is a compound based on Nylon 6 containing 20% Glass Fiber. Added feature of this grade is: Ellectrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Water Absorption | 1.0 % @Time 86400 sec |
1.0 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 107 MPa | 15500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 136 MPa | 19700 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 152 MPa | 22000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 112 µm/m-°C @Temperature 23.0 - 60.0 °C |
62.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 4.0 - 6.0 ohm | 4.0 - 6.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Eastman 7352 PET (discontinued **)
- Lehmann & Voss LUVOCOM® 1850-7783-1 PBT, with glass fiber, PTFE, lubricant modified
- Lubrizol Advanced Materials PEARLTHANE® 91T85 Thermoplastic Polyurethane Elastomer
- Solvay AQUARITE® ESL Surfactant
- A. Schulman POLYBATCH™ White 8350/UV5 Concentrate Based In Polyethylene
- Hexcel® HexTow™ 1925/AS Chopped Fiber
- Cytec Conathane® CC-1194 (Conap) Polyurethane Dielectric Conformal Coating
- Overview of materials for Polypropylene, Flame Retardant
- Fainplast Compounds FKA 97 Flexible PVC, Flame Retardant Insulation Lead Free
Copyright © lookpolymers.com All Rights Reserved