- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 196 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 196 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® EX39F ABS Highest impact extrusion ABS for sheet and blow molding applications. FDA food contact compliant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Cycolac® GPM5500S ABS (Europe-Africa-Middle East) CYCOLAC GPM5500S is a multi purpose injection moulding grade, equal to GPM5500 but equiped with anti static agents, providing a favourable balance of engineering properties. CYCOLAC GPM5500S has a w.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CM500LN Polypropylene, Impact Copolymer, High Flow, Medium Impact, Nucleated, Lube, Injection Molding COPYLENE™ CM500LN is a very high melt flow, medium impact polypropylene copolymer resin, designed for injection molding applications requiring a good balance of properties with faster cycling capab.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Eastman Tenite 371A-12 CAP Cellulose Acetate Propionate
(discontinued **) 12% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM D648 |
| LyondellBasell Pro-fax 6329 Polypropylene Homopolymer, Improved Chemical Resistance Key Features: improved chemical resistance polypropylene homopolymer resin, FDA acceptable, easier processingApplications: closures, housewares, chairsMeets FDA requirements in 21 CFR 177.1520 for a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Flint Hills 23S1Acs256 Random Copolymer Polypropylene Features: High contact clarity, blush resistant, good impact and flexural modulus. Product does not contain animal derived components.Applications: Blow molded articles - Food, health, medical an.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Flint Hills P9H9Z-018 Polypropylene Specialty polypropylene, UL certified, and FDA compliant.Applications: Extrusion coating.Former Huntsman polypropylene products are now produced by Flint Hills Resources. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 6.40 mm |
196 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical HIPS MI750L PS, Impact Modified Description: Injection Molding, PS, Impact Modified, High GlossApplication: Electric/Electronic Components, Stationary Articles, Food Containers, etc.CAS: 9003-55-8Information provided by LG Chemica.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 6.40 mm |
196 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LI970 Co-Extrusion ASA Description: Good Weatherability, Scratch ResistanceApplication: Window Profile, Siding, Rain GutterCAS: 26299-47-8Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.1 °C | 196 °F | Unannealed; ASTM D648 |
| Global PP-2512-H Polypropylene Block Copolymer Description-opacity, medium to high stiffness, high impact strength at low temperatureApplications-special for wire & cable, telecom insulationInformation provided by Global Polymers Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75B |
| Lucite International Diakon® LG156 Acrylic Bead Polymer, High Transparency PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite Inte.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Flint Hills P5M6N-058A Polypropylene Random Copolymer Features: Excellent processabilty, nucleated and antistat. Product does not contain animal derived components. Phthalate-free.Applications: Injection Molding: consumer disposable itemsInformation .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Ineos ABS Triax® 1120 ABS + Polyamide Blend (DAM) Key Features:UnfilledPlatableHigh impact or high impact modifiedSuitable processing methods:Injection moldingFilm extrusionBlow molding |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, Dry as Molded Injection molding grade with good flow and stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical damping be.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Ineos ABS Triax® KU 2-3050 ABS + Polyamide Blend (DAM) Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightHeat stabilized or stable to heatSuitable processing methods:Injection molding |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-LOY A3000 ABS LNP STAT-LOY* A3000 is a compound based on ABS resin. Added feature of this material is: Antistatic. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Unannealed; ASTM Data |
| Styron Magnum™ 348 ABS, Low Gloss MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75-2 |
| Borealis HK030U Polypropylene Compound HK030U is a special low viscosity polypropylene compound developed to fit the production of PP-GF composites in the direct LFT compression and injection molding process as well as in combination wit.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Method A; ASTM D648 |
| Chevron Phillips Marlex® K605 HDPE Blow Molding Resin Resin Type: Ethylene HomopolymerCharacteristics: Good ESCRExceptional rigidityExcellent melt strengthApplications: Automotive bumper beamsInformation provided by Chevron Phillips. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.1 °C | 196 °F | ISO 75-2/Bf |
| ExxonMobil Exxtral™ CNT 001W Performance Polyolefin Product Description: High impact, medium melt flow rate copolymer, colored black. Particularly suitable for injection molded automotive interior & exterior applications. Availability: North America .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75B |
| Dow INSPIRE™ 112 Performance Polymer INSPIRE™ 112 Performance Polymer is a propylene-based resin intended for use in film and sheet extrusion.Information provided by Dow |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.1 °C | 196 °F | ASTM D648 |
| Aclo Accucomp SAN SAN900L |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.1 °C | 196 °F | ASTM D648 |
| Aclo Accuguard Polypropylene HPN469V2CSL Homopolymer Non-Halogenated Copper Stabilized |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.1 °C | 196 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® ABS 922 NAT Availability: North AmericaForms: PelletsInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Ashley Polymers Ashlene® P268WO PPO An extrusion grade for general purpose application requiring flame retardancy and good impact resistance.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 6.40 mm |
196 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical HIPS MI750 PS, Impact Modified Description: Injection Molding, PS, Impact Modified, High GlossApplication: Electric/Electronic Components, Stationary Articles, Food Containers, etc.CAS: 9003-55-8Information provided by LG Chemica.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75-2 |
| Borealis Daplen™ KSX65T20 Polypropylene Compound 20% Mineral Filled Daplen KSX65T20 is a 20% mineral filled grade intended for injection molding. Daplen KSX65T20 has been developed especially for the car industry, to be used in interior parts. Daplen KSX65T20 offe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Eastman Tenite 383A-12 CAP Cellulose Acetate Propionate
(discontinued **) 12% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Braskem H 606 Thermoforming Polypropylene Description: H 606 is low melt flow rate homopolymer with general purpose additive package. This resin is designed for extrusion and thermoforming. H 606 presents excellent processability and high o.. |
|||