Chevron Phillips Marlex® K605 HDPE Blow Molding Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade |
| Manufacturer | Chevron Phillips Chemical Company LP |
| Trade Name | Marlex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chevron Phillips Marlex® K605 HDPE Blow Molding Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Resin Type: Ethylene HomopolymerCharacteristics: Good ESCRExceptional rigidityExcellent melt strengthApplications: Automotive bumper beamsInformation provided by Chevron Phillips.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 30 hour | 30 hour | Condition B; ASTM D1693 |
| 60 hour | 60 hour | Condition A; ASTM D1693 | |
| Melt Flow | 11 g/10 min | 11 g/10 min | Condition 190/21.6, HLMI; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | 750 % | 750 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 1.65 GPa | 239 ksi | Tangent, 16:1 span:depth,0.5in/min; ASTM D790 |
| Tensile Impact Strength | 240 kJ/m² | 114 ft-lb/in² | Type S bar; ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Method A; ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | Loading 1, Rate A; ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A, type 1 specimen; ASTM D746 |
Users viewing this material also viewed the following:
- Parker Chomerics PREMIER™ PEI-140 High Temperature Conductive Plastic for EMI Shielding
- LATI LAESTRA G/30 30% Glass Fiber Reinforced Syndiotactic Polystyrene (SPS) (discontinued **)
- SABIC Innovative Plastics LNP STAT-KON DEL22P PC (Asia Pacific)
- Teknor Apex APEX® 716 Polyvinyl Chloride, Flexible
- Eagle Brass 7026 Copper Nickel, Annealed
- EMS-Grivory Grivory® FG 34 NL nat 6023 PA6
- EMS-Grivory Grivory® TSG-50/4 PA666-GF50
- Eurostar Staramide 6 80E10 PA6, Injection Molded
- Eurostar Starpylen HW 30K ECR-BK PP, Injection Molded
Copyright © lookpolymers.com All Rights Reserved