Eastman Tenite 525-10 CAB Cellulose Acetate Butyrate (discontinued **)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Butyrate, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Tenite 525-10 CAB Cellulose Acetate Butyrate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 4.0 % | 4.0 % | |
| Tensile Modulus | 1.52 GPa | 220 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.45 J/cm² | 6.90 ft-lb/in² | |
| 0.420 J/cm² @Temperature -30.0 °C |
2.00 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 135 µm/m-°C @Temperature 20.0 °C |
75.0 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 137 µm/m-°C @Temperature 20.0 °C |
76.1 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | |
| Vicat Softening Point | 83.0 °C | 181 °F | |
| Glass Transition Temp, Tg | 102 °C | 216 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 215 - 230 °C | 419 - 446 °F |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit Teckshield®-F 50 OPI 0.001" Diameter Wire, Allycarbonate EMI Shielding Window
- Nilit FRIANYL A63 HS-GV35 Nylon 6.6 for injection molding, 35% glass fiber reinforced
- Solvay Specialty Polymers Mindel® B-430 Polysulfone, Modified (PSU, Modified) (discontinued **)
- Lehmann & Voss LUVOCOM® 1/GF/40/TF/13 Polyamide 66, with glass fiber and PTFE
- A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound
- Ensinger Tecatron® XP-72 Compression Molded PPS Compound, 20% PTFE Filled Natural
- China Tungsten YT772-2 Titanium Carbide and Nitride Based Carbides
- Solvay Specialty Polymers Veradel® AG-330 Polyethersulfone (PESU) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved