LG Chemical MU620 ABS, Low Deformation
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | LG Chemical MU620 ABS, Low Deformation.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Extrusion Molding, Low DeformationApplication: Mock-UpCAS No. 9003-56-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Extrusion Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm <br>@Thickness 3.20 mm |
0.0040 - 0.0070 in/in <br>@Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 25 g/10 min <br>@Load 10.0 kg,<br> Temperature 220 °C |
25 g/10 min <br>@Load 22.0 lb,<br> Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 104 | 104 | ASTM D785 |
| Tensile Strength, Yield | 37.3 MPa <br>@Thickness 3.20 mm |
5400 psi <br>@Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 25 % <br>@Thickness 3.20 mm |
25 % <br>@Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Yield | >= 5.0 % <br>@Thickness 3.20 mm |
>= 5.0 % <br>@Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 68.6 MPa <br>@Thickness 3.20 mm |
9960 psi <br>@Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa <br>@Thickness 3.20 mm |
370 ksi <br>@Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 3.14 J/cm <br>@Thickness 6.40 mm,<br> Temperature 23.0 °C |
5.88 ft-lb/in <br>@Thickness 0.252 in,<br> Temperature 73.4 °F |
ASTM D256 |
| 3.53 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 °C |
6.61 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C <br>@Thickness 6.40 mm |
196 °F <br>@Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C <br>@Thickness 6.40 mm |
183 °F <br>@Thickness 0.252 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 92.0 °C <br>@Load 5.00 kg |
198 °F <br>@Load 11.0 lb |
50°C/h; ASTM D1525 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 210 °C | 356 - 410 °F | Extrusion Molding |
| Zone 2 | 190 - 230 °C | 374 - 446 °F | Extrusion Molding |
| Zone 3 | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Zone 4 | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Adapter Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Die Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Roll Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Bottom, Extrusion |
| 70.0 - 90.0 °C | 158 - 194 °F | Middle, Extrusion | |
| 70.0 - 100 °C | 158 - 212 °F | Top, Extrusion | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Extrusion Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- NOVA Chemicals Dytherm® 150F Expandable Polystyrene
- SABIC Innovative Plastics LNP Faradex MS003XXC PP (Europe-Africa-Middle East)
- Mateck Cesium Iodide, CsI
- Gromax BTE90-DN001N1 Nylon 6 (Dry)
- Glastic Laminates/Shapes UTR Pultruded Tubing, Fiberglass-Reinforced Polyester
- SSAB Tunnplat Domex® 460MC HSLA Steel
- Styrolution Absolac® 300 ABS
- A. Schulman POLYBATCH™ Orange 1770E Concentrate Based In Polyethylene
- ChevronTexaco Journaltex® HD 57
Copyright © lookpolymers.com All Rights Reserved