SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527 |
| 32.0 MPa | 4640 psi | ASTM D638 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ASTM D638 |
| 37.0 MPa | 5370 psi | ISO 527 | |
| Elongation at Break | 21 % | 21 % | ASTM D638 |
| 32.2 % | 32.2 % | ISO 527 | |
| Elongation at Yield | 2.2 % | 2.2 % | ISO 527 |
| 2.6 % | 2.6 % | ASTM D638 | |
| Tensile Modulus | 1.94 GPa | 281 ksi | 1 mm/min; ISO 527 |
| 2.13 GPa | 309 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
| 63.0 MPa | 9140 psi | ISO 178 | |
| Flexural Modulus | 2.19 GPa | 318 ksi | ASTM D790 |
| 2.20 GPa | 319 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.43 J/cm | 15.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 96.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 95.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Piezo Kinetics 532 Lead Zirconate Titanate Piezoelectric
- Polykemi AB POLYfill PPH K20020 Polypropylene Homopolymer, Mineral Reinforced
- Arkema Group Kynar Flex® 2900 PVDF Copolymer (discontinued **)
- Isoflon PTFE +28% GL Blue-E glass-1% Blue Polytetrafluoroethylene with 28% GL-Blue-E glass-1% Blue (equivalent VX1)
- SABIC Innovative Plastics LNP LUBRICOMP Noryl_SPN422L PPE+PS
- Lubrizol ISOPLAST™ 202EZ Engineering Thermoplastic Polyurethane Resin
- ChevronTexaco Texcool® P 200
- 3M FM1542 Clear Polyester Label Products
- ExxonMobil Escorene® LD-332 EVA Packaging Film Resin, High Clarity (discontinued **)
Copyright © lookpolymers.com All Rights Reserved