- Dow INSPIRE™ 112 Performance Polymer
Dow INSPIRE™ 112 Performance Polymer
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Dow Chemical |
| Trade Name | INSPIRE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow INSPIRE™ 112 Performance Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INSPIRE™ 112 Performance Polymer is a propylene-based resin intended for use in film and sheet extrusion.Information provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 | 61 | ISO 868 |
| Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ISO 527 |
| Film Tensile Strength at Yield, MD | 29.0 MPa | 4210 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 24.0 MPa | 3480 psi | ISO 527-3 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527 |
| Film Elongation at Break, MD | 600 % | 600 % | ISO 527-3 |
| Film Elongation at Break, TD | 710 % | 710 % | ISO 527-3 |
| Elongation at Break | 25 % | 25 % | ISO 527 |
| Elongation at Yield | 14 % | 14 % | ISO 527 |
| Tensile Modulus | 1.15 GPa | 167 ksi | ISO 527 |
| Flexural Modulus | 1.35 GPa | 196 ksi | ISO 527 |
| Secant Modulus, MD | 1.10 GPa | 160 ksi | 1% Secant; ISO 527-3 |
| Secant Modulus, TD | 0.950 GPa | 138 ksi | 1% Secant; ISO 527-3 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -20.0 °C |
5.71 ft-lb/in² @Temperature -4.00 °F |
ISO 180 |
| 23.0 kJ/m² @Temperature -10.0 °C |
10.9 ft-lb/in² @Temperature 14.0 °F |
ISO 180 | |
| 46.0 kJ/m² @Temperature 23.0 °C |
21.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Dart Drop Test | 170 g | 0.375 lb | Method A; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 52.0 MPa | 7540 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 39.0 MPa | 5660 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 164 °C | 327 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75B |
| Vicat Softening Point | 148 °C | 298 °F | ISO 306A |
| Shrinkage | 1.5 % | 1.5 % | ISO 2577 |
Users viewing this material also viewed the following:
- Oceanchem Group Xanthan Gum Oil Drilling Grade
- Rotuba M Cellulose Acetate
- KKPC KOSYN 1721 Styrene Butadiene Rubber
- Indorama Auriga Polymers Polyclearâ„¢ Refresh 1101 PET Resin
- Styron CALIBREâ„¢ 891 20 Polycarbonate, General Purpose
- The NanoSteel® Company SHS 9800 Steel Alloy, Wear Plate
- Toyobo A2080A Thermoplastic Polyurethane Elastomer, Injection Grade
- DuPont Performance Polymers Rynite® 530 BK503 Polyethylene Terephthalate (PET) (Unverified Data**)
- BorsodChem ONGRONOX EHP 75 D peroxide-type initiator
- P & P Technology MW Series Conductive Fabric
Copyright © lookpolymers.com All Rights Reserved