- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 259 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 259 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 259 - 272 °C | 498 - 522 °F | Average value: 265 °C Grade Count:3 |
| Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 20% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 20% Glass Reinforced". Each property range of values reported is minimum and maximum values.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C @Thickness 3.20 mm |
498 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL16 PA 66 LNP* LUBRICOMP* RFL16 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C @Thickness 3.20 mm |
498 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp RFN18SXZ PA 66 LNP LUBRICOMP* RFN18SXZ is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Ameri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF25 L BK 25% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 25% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Lubricated and Heat StabilizedAppearanc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF30 HR L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized, Lubricated and Hydroly.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF33 HR L 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: LubricantFeatures: Lubricated and Hydrolysis Resistant TPCI# 9357101Informatio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF33 L BKN001 33% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearanc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF33 NAT001 Y 33% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedUL File N.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF40 HS L BK 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedUL File N.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF40 UV L BK 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Lubricant and UV StabilizerFeatures: Lubricated and Good UV ResistanceAppearan.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF43 HS L BK001 43% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 43% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearanc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF45 L BK 45% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 45% Filler by WeightAdditive: Lubricant Features: Lubricated Appearance: BlackProcessing Method: Injection M.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 CF10 TS15 BK 10% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightAdditive: PTFE Lubricant(13%) and Silicone Lubricant(2%)Features: Lubricated Appearance: BlackInforma.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 CF30 TL15 BK 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%) Features: Lubricated, Good Wear Resistance and Low Friction Appearance.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF10 TL10 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(5%)Features: Lubricated, Good Wear Resistance, Low Fricti.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF30 TL15 BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Low Frict.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF30 TL15 UV 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer, UV Stabilizer and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resist.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF30 TL5 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Low Frict.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF33 TL15 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Heat Stab.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF40 TL10 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 40% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(10%)Features: Lubricated and Heat StabilizedInformation p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP RF008 PA 66 LNP* THERMOCOMP* RF-1008 is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP RF009S PA 66 LNP* THERMOCOMP* RF009S is a compound based on Nylon 66 resin containing 45% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C @Thickness 3.20 mm |
498 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOTUF RF006I PA 66 LNP* Thermotuf* RF006I is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PA6/6 GF40 FR HS L 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 40% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Flame Retardant, Lubricated and Heat StabilizedInform.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C @Thickness 3.20 mm |
498 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Verton RV008ESV_GY7E072 PA 66 Preliminary data for 40% long glass fiber filled, single color pellet gray, PA66This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP VERTON RV00AEU PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AEU is a compound based on PA 66 resin containing Long Glass Fiber. Added features include : Easy Molding, UV Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | ISO 75 |
| Polyram PlusTek PA4501G6 Nylon 66, 30% Glass Fiber Reinforced, Low Friction 30% Glass fiber reinforced Nylon 66 for low friction applications.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | ISO 75 |
| Polyram PlusTek PA4802G6BK10 Nylon 66 for Injection Molding, 30% Glass Fiber Reinforced, PTFE Lubricated 30% Glass fiber reinforced, PTFE lubricated Nylon 66 for injection molding application.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON OE002 PPS - LINEAR LNP* STAT-KON* OE002 is a compound based on PPS - Linear resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C @Thickness 3.20 mm |
498 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON RV0079 PA 66 LNP VERTON* RV0079 is a compound based on Nylon 66 resin containing 35% Long Glasss Fiber. Added features of this material include: Flame Retardant, Structural. |
|||