- Techmer ES Luriblend® PA6/6 GF33 TS15 BK 33% Glass Filled
Techmer ES Luriblend® PA6/6 GF33 TS15 BK 33% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Heat Stabilized , Nylon 66, PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6/6 GF33 TS15 BK 33% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Heat Stabilizer, Silicone Lubricant and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Heat Stabilized and Low Friction Appearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm |
0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 147 MPa | 21300 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 221 MPa | 32000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.17 mm |
1.40 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.28 | 0.28 | ASTM D1894 |
| Coefficient of Friction, Static | 0.22 | 0.22 | ASTM D1894 |
| K (wear) Factor | 36.3 x 10-8 mm³/N-M | 18.0 x 10-10 in³-min/ft-lb-hr | |
| Limiting Pressure Velocity | 0.596 MPa-m/sec | 17000 psi-ft/min | 10 fpm |
| 0.596 MPa-m/sec | 17000 psi-ft/min | 1000 fpm | |
| 0.666 MPa-m/sec | 19000 psi-ft/min | 100 fpm |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 21.7 kV/mm | 550 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Overview of materials for Nylon 11 with 10% Glass Fiber Filler
- Materion BrushBronze® 95510 (AMS 4880) Continuous Cast 4.0" - 17.0"
- Michelman® Michem® Emulsion 66035 Anionic paraffin/polyethylene wax emulsion
- LG Chemical XR404HJ ABS, Heat Resistance, Curl Fit
- Elastocon TPE Technologies Elastocon® 2810 Thermoplastic Elastomer
- DSM Novamid® 1011CH5KR PA6
- AK Steel ASTM A 607 Class 2 Formable, Grade 50K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
- Beijing Evergrow Resources BF-6 Basalt Needle Felt
- DuPont Performance Polymers Delrin® FG150 NC010 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved