SABIC Innovative Plastics LNP Lubricomp RFN18SXZ PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber/MoS2 Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp RFN18SXZ PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RFN18SXZ is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| 1.51 g/cc | 0.0546 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 23°C / 50% RH; ISO 62 |
| 0.61 % @Time 86400 sec |
0.61 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0035 cm/cm @Time 86400 sec |
0.0035 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0117 cm/cm @Time 86400 sec |
0.0117 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 177 MPa | 25700 psi | ASTM D 638 |
| 192 MPa | 27800 psi | ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D 638 |
| 2.2 % | 2.2 % | ISO 527 | |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 1 mm/min; ISO 527 |
| 15.51 GPa | 2250 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 268 MPa | 38900 psi | ASTM D 790 |
| 287 MPa | 41600 psi | ISO 178 | |
| Flexural Modulus | 10.75 GPa | 1559 ksi | ASTM D 790 |
| 13.1 GPa | 1900 ksi | ISO 178 | |
| Izod Impact, Notched | 0.840 J/cm @Temperature 23.0 °C |
1.57 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 8.91 J/cm @Temperature 23.0 °C |
16.7 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 59.0 kJ/m² @Temperature 23.0 °C |
28.1 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.75 | 0.75 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.59 | 0.59 | ASTM D 3702 Modified |
| K (wear) Factor | 90.6 x 10-8 mm³/N-M | 45.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C @Thickness 3.20 mm |
498 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 250 °C @Thickness 3.20 mm |
482 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP EIP2012 F Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE
- PolyOne Synprene® RT-3750 Styrene Butadiene Block Copolymer (SBC) with Mineral Filler (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP SCL36 PA12
- Shakespeare NX-811 Economy Nylon Copolymer Fishing Line, 4 lb
- Zell-Metall Engineering Plastics Zellamid 202 (PA 6) at 50% RH
- DSM Stanyl® 46HF4130 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Cond)
- EMS-Grivory Grivory® GV-4 FWA black 9225 PA*-GF40
- Bapolene® 3295 Polyethylene, Injection Grade
- Lanxess Pocan® DP T 7140 LDS 000000 PBT + PET, 44% Mineral + L227Glass Fiber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved