Techmer ES HiFill® PA6/6 GF45 TL10 45% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled , Nylon 66, PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PA6/6 GF45 TL10 45% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 45% Filler by WeightAdditive: PTFE Lubricant (10%)Features: LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Water Absorption | 0.60 % @Time 86400 sec |
0.60 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm |
0.0040 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 181 MPa | 26200 psi | ASTM D638 |
| 131 MPa @Temperature 93.3 °C |
19000 psi @Temperature 200 °F |
ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 296 MPa | 43000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| 8.96 GPa @Temperature 93.3 °C |
1300 ksi @Temperature 200 °F |
ASTM D790 | |
| Izod Impact, Notched | 1.17 J/cm @Thickness 3.17 mm |
2.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 15.5 J/cm @Thickness 3.17 mm |
29.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.8 µm/m-°C | 41.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8923E (717P) (UF) Synthetic Oil
- Precision Polymer Engineering E63B Ethylene Propylene Rubber
- M Chemical GUARD DOGâ„¢ UV360 Light Absorber
- Lubrizol Advanced Materials PEARLTHANE® 15N95UV Thermoplastic Polyurethane Elastomer
- Unipetrol A+ High-Conductive Carbon Black Chezacarb
- Universal Wire Works 901 (AMS 5830) Filler Metal
- A. Schulman POLYBATCH™ Silver 70100 Concentrate Based In LDPE
- Arlon R37230R006 0.006" (0.152 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Substrate
- Braskem Idealis 500 Compression Molding High Molecular Weight Polyethylene
Copyright © lookpolymers.com All Rights Reserved