Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 20% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polycyclohexylenedimethylene Terephthalate (PCT) , Polycyclohexylenedimethylene Terephthalate (PCT), 20% Glass Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 20% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 20% Glass Reinforced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.14 - 1.58 g/cc
0.0412 - 0.0571 lb/in³
Average value: 1.42 g/cc Grade Count:7
Filler Content 20.0 %
20.0 %
Average value: 20.0 % Grade Count:4
Linear Mold Shrinkage 0.00300 - 0.00600 cm/cm
0.00300 - 0.00600 in/in
Average value: 0.00433 cm/cm Grade Count:3
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 62.0 - 100 MPa
8990 - 14500 psi
Average value: 93.8 MPa Grade Count:7
Elongation at Break 1.80 - 3.30 %
1.80 - 3.30 %
Average value: 2.34 % Grade Count:7
Modulus of Elasticity 5.50 - 8.00 GPa
798 - 1160 ksi
Average value: 7.05 GPa Grade Count:6
Flexural Yield Strength 97.0 - 155 MPa
14100 - 22500 psi
Average value: 142 MPa Grade Count:7
Flexural Modulus 4.00 - 7.40 GPa
580 - 1070 ksi
Average value: 5.96 GPa Grade Count:7
Izod Impact, Notched 0.320 - 1.10 J/cm
0.600 - 2.06 ft-lb/in
Average value: 0.618 J/cm Grade Count:4
0.32034 - 1.00 J/cm

@Temperature -40.0 - -40.0 °C
0.60013 - 1.87 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 0.660 J/cm Grade Count:2
Izod Impact, Unnotched 2.56 - 430 J/cm
4.80 - 806 ft-lb/in
Average value: 112 J/cm Grade Count:4
2.1356 - 2.1356 J/cm

@Temperature -40.0 - -40.0 °C
4.0009 - 4.0009 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 2.14 J/cm Grade Count:1
Izod Impact, Notched (ISO) 5.00 - 8.00 kJ/m²
2.38 - 3.81 ft-lb/in²
Average value: 5.83 kJ/m² Grade Count:6
Charpy Impact Unnotched 3.00 - 5.00 J/cm²
14.3 - 23.8 ft-lb/in²
Average value: 3.50 J/cm² Grade Count:6
3.00 - 3.00 J/cm²

@Temperature -30.0 - -30.0 °C
14.3 - 14.3 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 3.00 J/cm² Grade Count:1
Charpy Impact, Notched 0.500 - 0.850 J/cm²
2.38 - 4.05 ft-lb/in²
Average value: 0.608 J/cm² Grade Count:6
0.700 - 0.700 J/cm²

@Temperature -30.0 - -30.0 °C
3.33 - 3.33 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 0.700 J/cm² Grade Count:1
Thermal Properties Metric English Comments
Melting Point 283 - 285 °C
541 - 545 °F
Average value: 284 °C Grade Count:6
Deflection Temperature at 0.46 MPa (66 psi) 259 - 272 °C
498 - 522 °F
Average value: 265 °C Grade Count:3
Deflection Temperature at 1.8 MPa (264 psi) 194 - 256 °C
381 - 493 °F
Average value: 232 °C Grade Count:7
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:5
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Average value: 1.00e+15 ohm-cm Grade Count:3
Surface Resistance 1.00e+15 - 1.00e+17 ohm
1.00e+15 - 1.00e+17 ohm
Average value: 3.70e+16 ohm Grade Count:3
Dielectric Strength 19.7 - 41.0 kV/mm
500 - 1040 kV/in
Average value: 27.1 kV/mm Grade Count:3
Processing Properties Metric English Comments
Melt Temperature 295 - 310 °C
563 - 590 °F
Average value: 302 °C Grade Count:7
Mold Temperature 80.0 - 175 °C
176 - 347 °F
Average value: 121 °C Grade Count:5
Drying Temperature 95.0 - 150 °C
203 - 302 °F
Average value: 106 °C Grade Count:7
Moisture Content 0.0300 %
0.0300 %
Average value: 0.0300 % Grade Count:6