SABIC Innovative Plastics LNP THERMOCOMP RF008XXH PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF008XXH PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF008XXH is a compound based on Nylon 66 resin containing 40% Glass Fiber. Added feature of this material includes: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.660 % | 0.660 % | 50% RH, 24 hrs; ASTM D570 |
| 1.00 % | 1.00 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 210 MPa | 30500 psi | Type I, 5 mm/min; ASTM D638 |
| 232 MPa | 33600 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D638 |
| 2.9 % | 2.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 13.9 GPa | 2020 ksi | 5 mm/min; ASTM D638 |
| 14.06 GPa | 2039 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 229 MPa | 33200 psi | ISO 178 |
| 337 MPa | 48900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 11.17 GPa | 1620 ksi | 2 mm/min; ISO 178 |
| 12.4 GPa | 1800 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.66 J/cm | 3.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.2 J/cm | 24.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 86.0 kJ/m² | 40.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 18.0 J @Temperature 23.0 °C |
13.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 244 °C | 471 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Overview of materials for Polystyrene, Wood Filled
- Gwent Electronic Materials P2121112P8 Argon Plasma Modified Multiwalled Carbon Nanotubes
- Taiwan PU Corporation TPUI-ED64 General Grade, Injection Molding Polyester Base TPU
- SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP STAT-KON FD000 PE
- SABIC Innovative Plastics Xylex X8300HP PC+POLYESTER (Europe-Africa-Middle East)
- Total HDPE B5845 High Density Polyethylene - Blow Molding Resin
- 3M FM002 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- Elisto THERMOSTAR® LD 500 Frame Press Insulation Material
Copyright © lookpolymers.com All Rights Reserved