SABIC Innovative Plastics LNP LUBRICOMP RFL16 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFL16 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RFL16 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.570 % | 0.570 % | 50% RH, 24 hrs; ASTM D570 |
| 0.880 % | 0.880 % | 23°C / 50% RH; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 185 MPa | 26800 psi | 5 mm/min; ISO 527 |
| 189 MPa | 27400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 188 MPa | 27300 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 |
| 2.7 % | 2.7 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 10.63 GPa | 1542 ksi | 1 mm/min; ISO 527 |
| 11.02 GPa | 1598 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 263 MPa | 38100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.92 GPa | 1290 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.98 GPa | 1300 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.18 J/cm | 2.21 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.3 J/cm | 21.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 62.0 kJ/m² | 29.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.55 | 0.55 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.53 | 0.53 | ASTM D3702 Modified |
| K (wear) Factor | 32.2 x 10-8 mm³/N-M | 16.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.5 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 91.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 259 °C @Thickness 3.20 mm |
498 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 251 °C | 484 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 249 °C @Thickness 3.20 mm |
480 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® LG8002 PC+ABS
- Parker Chomerics CHO-SEAL E6306 Conductive Elastomer
- NIZHNEKAMSKNEFTEKHIM PE 4026Z (26460) Linear Low Density Polyethylene
- Parker Chomerics SOFT-SHIELD® 5500 EMI Shielding and Grounding Gasket
- Minelco FordaTal Talc
- SABIC Innovative Plastics LNP LUBRICOMP OCP36F PPS - Linear
- SGL Carbon Group SIGRAFIL C® C25 S006 GLY Staple Carbon Fiber, Glycerine Sizing
- SABIC Innovative Plastics LNP LUBRILOY U2000A PPA (Asia Pacific)