SABIC Innovative Plastics LNP THERMOCOMP 4X08423 FP-P (PFA)
| Category | Polymer , Thermoplastic , Fluoropolymer , PFA |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 4X08423 FP-P (PFA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* 4X08423 is a compound based on PFA resin containing Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.20 g/cc | 2.20 g/cc | ASTM D792 |
| Density | 2.20 g/cc | 0.0795 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 |
| 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
| 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ISO 527 |
| 3.6 % | 3.6 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D638 |
| 3.3 % | 3.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.60 GPa | 667 ksi | 1 mm/min; ISO 527 |
| 4.67 GPa | 677 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
| Flexural Yield Strength | 49.0 MPa | 7110 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.30 GPa | 479 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.37 GPa | 634 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 2.59 J/cm | 4.85 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.93 J/cm | 11.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
28.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 89.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
49.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 297 °C @Thickness 3.20 mm |
567 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 243 °C @Thickness 3.20 mm |
469 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S65A Silicone Rubber
- Premix Thermoplastics PRE-ELEC® PE 1296 Conductive Thermoplastic Compound
- PolyOne Geon™ Vinyl Flexible R7545H Polyvinyl Chloride, Flexible (PVC, Flexible)
- M. Holland Company CP700 Polypropylene Copolymer
- Indium Corp. Indalloy 102 Bismuth-Lead-Tin Solder Alloy
- Michelman® Micryl™ 783 Water resistant coating
- Sibur BSK-1500 Styrene-Butadiene Rubber (SBR)
- Esstech V-117-1095 Barium Borosilicate Glass
- Gharda Chemicals Gafone S 1500 Polysulfone (PS) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved