- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 230 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 230 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75/2Bf |
| Radici Radilon® AERV1906 LK (dry) Nylon 66 Glass-fiber reinforced with high impact strength, heat stabilizedInformation provided by Radici group. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Conditioned 50% RH; ISO 75 |
| Manifattura Cattaneo PA 6.6 Nylon Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C @Thickness 6.40 mm |
446 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUMID GP3200B(W) PA66+MF20%, General Purpose Feature: Injection Molding, PA6+MF20%, General PurposeApplication: E&E (Rice Cooker Housing)Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | DAM |
| Aardvark Polymers Aarlon® 4055FR PA 6/6 Rotational Molding Resin Aarlon 4055FR is a premium flame retardant type 6/6 nylon.Aarlon 4055FR is halogen, heavy metal, and red phosphorus free.Aarlon 4055FR is UL94 V-0 rated.Aarlon 4055FR is semi-crystalline, nucleated,.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C @Thickness 6.40 mm |
446 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa PET-RG15 Flame Retardant, 15% Glass Fiber Reinforced PET Features:Flame retardantHigh strengthGood heat resistanceOutstanding electrical propertiesApplications:Injection moldingConnectorsRelayBobbinsSocketsE & E partsInformation Provided by Kingfa Sci. & .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75 |
| Solvay TECHNYL® A 52 G1 MX 20 PA66, Eh 0 Description: TECHNYL A 52 G1 MX20 is a Polyamide 6.6 glow wire resistant, reinforced with mineral fillerColors: it is marketed in black color.Available in: Latin AmericaMain Properties: ?Glow wire r.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C @Thickness 3.20 mm |
446 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66 (Asia Pacific) LNP* Stat-loy* 9X03508 is a compound based on PPO+PA66 resin containing Flame Retardant, Anti-Static. Added features of this material include: Antistat, Flame Retardant, High Impact. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Samyang Tribit® 1500G30 Polybutylene Terephthalate, 30% Glass Reinforced Characteristics:G/F reinforcedHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A partsAll infor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Absolute Drying; ASTM-D648 |
| Toyobo GLAMIDE® T-662 Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Toyobo T-661 Nylon 66, Standard Grade (DAM) Features: Non-reinforced, Standard GradeInformation provided by Toyobo. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Cheng Yu Plastic N66C1 Nylon 66, 10% Mineral Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Cheng Yu Plastic N6G20 Nylon 6, 20% Glass Filled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Cheng Yu Plastic NGCV2 Flame Retardant Nylon 6, 20% Mineral Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 179 |
| CP-Polymer-Technik Wellamid® 6600/50 GV 15 HWCP 15% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | DAM; ASTM D648 |
| DuPont Performance Polymers Zytel® FR7025V0F NC010 Nylon 66
(Unverified Data**) Zytel® FR7025V0F NC010 is a flame retardant polyamide 66 resin for injection molding. It does not contain elemental phosphorous, halogens or heavy metals.Information provided by DuPont Performance.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Eurostar Staramide A40 PA66, Extrusion Staramide A40 is Unreinforced, High Viscosity Polyamide 66, Extrusion ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| E-Polymers TEKAMID® TA210HS , Heat Stabilized PA66, DAM Heat stabilizedInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| E-Polymers TEKAMID® TA210L Lubricated PA66, DAM LubricatedInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75-1/-2 |
| DSM Akulon® S223-DK Nylon 66 (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Unannealed; ISO 75-2/B |
| Ascend Performance Materials Vydyne® 20NSP Nylon 66, DAM Vydyne® 20NSP is a general-purpose, highly nucleated, lubricated PA66 resin available in natural color. It is designed to crystallize rapidly in order to reduce cycle times and increase productivit.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 614 Nylon 6, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Dry; ASTM D648 |
| Asahi Kasei Leona® 1300S Nylon 66 General purpose grade. Good balance of flowability and mechanical properties.Applications:Connectors, washers, cable ties. Information provided by Asahi Kasei |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Dry; ASTM D648 |
| Asahi Kasei Leona® 1502 Nylon 66 Similar to 1500 but with improved heat aging resistance.Applications:Under-the-hood automotive parts Information provided by Asahi Kasei |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 638 Nylon 6/6, Mineral Reinforced, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company.35% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75-2/B |
| Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Dry as Molded Vydyne® R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 - 245 °C | 446 - 473 °F | Average value: 241 °C Grade Count:21 |
| Overview of materials for Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant". Each property range of values re.. |
|||