- Radici Radilon® AERV1906 LK (dry) Nylon 66
Radici Radilon® AERV1906 LK (dry) Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | Radici Group Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Radici Radilon® AERV1906 LK (dry) Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass-fiber reinforced with high impact strength, heat stabilizedInformation provided by Radici group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527-1/2 |
| Elongation at Break | 6.2 % | 6.2 % | ISO 527-1/2 |
| Elongation at Yield | 3.2 % | 3.2 % | ISO 524-1/2 |
| Tensile Modulus | 5.05 GPa | 732 ksi | ISO 527-1/2 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 3.95 GPa | 573 ksi | ISO 178 |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.15 J/cm² | 5.47 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 1135 7-1-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75/2Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75/2Af |
| Vicat Softening Point | 235 °C | 455 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
Users viewing this material also viewed the following:
- Plansee MW30 Molybdenum-Tungsten
- DuPont Bynel® 4003 Anhydride-Modified HDPE Adhesive Resin (discontinued **)
- Overview of materials for High Density Polyethylene (HDPE), Carbon Black Filled
- Greene Tweed Xycomp® 1001-01 PEEK, Carbon Fiber Filled
- Lehmann & Voss LUVOCOM® 1-0890 Polyamide 66, with carbon fiber, low-warpage, heat stabilized
- Shin-Etsu Silicones C-19A Silicone Gum
- Chesterton ARC BX1 Sliding Wear Compound
- BASF Ultramid® A3WGM53 BK20560 25/15% Glass/Mineral Filled PA66 (Conditioned)
- Carpenter Custom 455® Stainless Steel, Annealed, 1.27 mm Strip
- Polyram RamSter PF321G4 PBT, 20% Glass Fiber, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved