Aardvark Polymers Aarlon® 4055FR PA 6/6 Rotational Molding Resin
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Gehrig & Associates |
| Trade Name | Aarlon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aardvark Polymers Aarlon® 4055FR PA 6/6 Rotational Molding Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aarlon 4055FR is a premium flame retardant type 6/6 nylon.Aarlon 4055FR is halogen, heavy metal, and red phosphorus free.Aarlon 4055FR is UL94 V-0 rated.Aarlon 4055FR is semi-crystalline, nucleated, and heat stabilized.Aarlon 4055FR is available in natural and may be colored and/or printed.Aarlon 4055FR is applicable for industrial markets such as automotive, aerospace, and electronics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | DAM |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 1.57 mm |
0.0080 in/in @Thickness 0.0620 in |
DAM |
| 0.011 cm/cm @Thickness 3.17 mm |
0.011 in/in @Thickness 0.125 in |
DAM | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 1.60 mm |
0.0080 in/in @Thickness 0.0630 in |
DAM |
| 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
DAM |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 89.2 MPa | 12900 psi | DAM |
| Elongation at Break | 14 % | 14 % | DAM |
| Flexural Modulus | 3.43 GPa | 497 ksi | DAM |
| Izod Impact, Unnotched | 0.430 J/cm | 0.806 ft-lb/in | DAM |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | DAM |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | DAM |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM |
| UL RTI, Electrical | 130 °C @Thickness 1.50 mm |
266 °F @Thickness 0.0591 in |
DAM |
| 130 °C @Thickness 3.00 mm |
266 °F @Thickness 0.118 in |
DAM | |
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 1.50 mm |
167 °F @Thickness 0.0591 in |
DAM |
| 75.0 °C @Thickness 3.00 mm |
167 °F @Thickness 0.118 in |
DAM | |
| UL RTI, Mechanical without Impact | 85.0 °C @Thickness 1.50 mm |
185 °F @Thickness 0.0591 in |
DAM |
| 85.0 °C @Thickness 3.00 mm |
185 °F @Thickness 0.118 in |
DAM | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
DAM, Test 1 |
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
DAM, Test 2 | |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
DAM, Test 1 | |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
DAM, Test 2 | |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
DAM, Test 1 | |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
DAM, Test 2 |
Users viewing this material also viewed the following:
- PolyOne Maxxam® FR PE JR 165 High Density Polyethylene (HDPE) (discontinued **)
- Shakespeare FN-29 Freshwater Nylon Copolymer Fishing Line, 30 lb
- Polyram RamTal PMH2003 Polyacetal Homopolymer for Injection Molding
- Williams Advanced Alloys WS361 Solder
- Dow Nordel® IP 4570 EPDM Hydrocarbon Rubber
- Carmel Olefins CAPILENE® QW 73 AV Propylene Random Copolymer
- BASF Pluracol® 4156 Slabstock Foam Polyol
- Colorite Polymers 7075 General Purpose Vinyl Compound
- ExxonMobil CM-L Mobilgrease CM Series
- Buckeye Polymers BP RPP 2012 T NAT Polypropylene, Calcium Carbonate Filled
Copyright © lookpolymers.com All Rights Reserved