A. Schulman ComAlloy Hiloy® 638 Nylon 6/6, Mineral Reinforced, Flow Enhanced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 638 Nylon 6/6, Mineral Reinforced, Flow Enhanced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.35% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 78.0 MPa | 11300 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.01 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | Approximate middle barrel temperature. |
Users viewing this material also viewed the following:
- Indium Corp. Indalloy 212 Ag-Cu-Zn-Cd Solder Alloy
- KaMin Polyplate® HMT Kaolin Clay - Delaminated
- Ineos L70Z-01 Polypropylene Impact Copolymer
- Lanxess Pocan® DP 7318 000000 PBT, 17% Pigment
- SABIC Innovative Plastics NORYL ZM3640 PPE+PS (Asia Pacific)
- Saint-Gobain Norton® Fluorglas® Chemfilm® R167 Extruded Expanded PTFE Film (0.006" thick)
- Teknor Apex Sinvicomp SFE 7000 Polyvinyl Chloride, Flexible
- UBE UBESTA® 3030JLX1 8x1 mm Black Automotive Grade Nylon 12 Tube
- Cytec Thornel® Mat VMA Carbon Fiber
- Akro-Plastic Akromid® B3 GF 25 (2471) PA 6 Conditioned, 25% Glass Filled
Copyright © lookpolymers.com All Rights Reserved