E-Polymers TEKAMID® TA210L Lubricated PA66, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer E-Polymers Co. Ltd.
Trade Name TEKAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers TEKAMID® TA210L Lubricated PA66, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LubricatedInformation provided by E-Polymers Co. Ltd.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ASTM D792
Water Absorption 1.3 %
1.3 %
23°C/24 hr; ASTM D570
Linear Mold Shrinkage 0.015 cm/cm
0.015 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 78
78
ASTM D786
Hardness, Rockwell R 120
120
ASTM D786
Hardness, Shore D 79
79
Tensile Strength, Yield 85.0 MPa
12300 psi
ASTM D638
Elongation at Break 50 %
50 %
ASTM D638
Flexural Yield Strength 117 MPa
17000 psi
ASTM D790
Flexural Modulus 3.00 GPa
435 ksi
ASTM D790
Izod Impact, Notched 0.550 J/cm
1.03 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB

@Thickness 3.20 mm
 NB

@Thickness 0.126 in
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 20.0 °C
 38.9 µin/in-°F

@Temperature 68.0 °F
 ASTM D696
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
Melting Point 260 °C
500 °F
ASTM D2133
Deflection Temperature at 0.46 MPa (66 psi) 230 °C
446 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
ASTM D648
Flammability, UL94 V-2
V-2
Electrical Properties Metric English Comments
Arc Resistance 190 sec
190 sec
Tungsten electrode; ASTM D495
Processing Properties Metric English Comments
Processing Temperature 270 - 280 °C
518 - 536 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F