- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 108 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 108 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CQX8025 R2 Polypropylene, Mineral Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 - 215 °C | 226 - 419 °F | Average value: 170 °C Grade Count:31 |
| Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled". Each property range of values repor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| Flint Hills AP5206-HN Polypropylene Impact Copolymer Features: Nucleated for fast cycle and good mold release. Product does not contain animal derived components.Applications: Compression and injection molding: caps and closuresInformation Provided b.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| Flint Hills P4C5B-075 Homopolymer Polypropylene Homopolymer, and FDA compliant.Features: Nucleated, antistat, and controlled rheology.Applications: Injection molding: tape extrusion and closures.Former Huntsman polypropylene products are now prod.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-9000 MA B Polypropylene Copolymer INNOPOL® CS 2-9000 MA B is a black colored, high melt flow copolymer with antistatic additive.INNOPOL® CS 2-9000 MA B is developed for producing injection molded automotive components.All info.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| MRC Polymers NAXALOYâ„¢ 780 GF11 PC+PBT Polyester Blend, 11% Glass Fiber Filled Good chemical resistance, impact and heat resistanceAvailable in Black OnlyCan be UV StabilizedInternal and external lubricant can be added.Information provided by MRC Polymers Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa PBT-RG002 Flame Retardant PBT Features:Flame retardantGood chemical resistanceOutstanding surfaceEasy processingHigh impactApplications:Injection moldingConnectors, terminal blocksRelay, switchBobbinsPlugsE & E partsInformation .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical XR404 ABS, Heat Resistance Feature: Injection Molding, Heat ResistanceApplication: Electric & Electronic Housing (Frame etc) Automotives Interior & Exterior Housing (Garnish etc)CAS No. 25120-20-1, 9003-56-9 and 25747-74-7Inf.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical XR404HJ ABS, Heat Resistance, Curl Fit Feature: Injection Molding, Heat Resistance, Curl FitApplication: Automotives Interior Housing (P/W Switch Housing Etc)CAS No. 25120-20-1, 9003-56-9 and 25747-74-7Information provided by LG Chemica.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 7985 PP SABIC® PPcompound 7985 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with interior automotive UV stability. The IMDS is 2097.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® GA-4025 ABS, 25% Glass Filled Permanent static prevention material with 25% GF reinforcement that can be used in OA device and trayInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® GR-4020 ABS, 20% Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® GR-4030 ABS, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL PPX PPX7110 PPE+PP (Europe-Africa-Middle East) PPX7110 is an alloy of PP and PPO, providing high impact and good heat resistance. Generic identification acc. ISO11469: >PP+PPE+PS-I |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU Toyota is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene DescriptionPolypropylene PP 2175 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene DescriptionPolypropylene PP 2175 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 2175HU-31 High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU-31 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU Toyota is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene DescriptionPolypropylene PP 2175 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene DescriptionPolypropylene PP 2175 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 2175HU-31 High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU-31 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ISO 75-1/-2 |
| Covestro Bayblend® FR 3011 Polycarbonate + ABS, Flame Retardant Grade Injection molding gradegood flowhigh heat resistanceVicat/B 120 temperature = 118 °CUL-listing 94 V-0 (1.5 mm) antimony-, chlorine- and bromine-free flame retardantglow wire test (GWFI): 960 °.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| Carmel Olefins CAPILENE® W 77 AV Polypropylene Homopolymer CAPILENE® W 77 AV is a very high melt flow rate polypropylene homopolymer for injection molding with antistatic and nucleating additives. It offers a good balance of stiffness and flow, high de-mol.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| Aaron Industries AVPS M 100-2 Virgin Polystyrene Melt flow index may be specified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Ascend Performance Materials VYDYNE® 45 Nylon, Impact Modified, Weather Stable Typical property data. VYDYNE is a registered trademark of Solutia Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | |
| Arkema Group Appryl® CZT 1030 Polypropylene, 30% Talc/Mica Filled Compound of a PP copolymer modified with EPR and 30% of a mixture of talc and mica. This grade has been specially developed for exterior automotive applications, that required an excellent thermal d.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| Cheng Yu Plastic A706G15 SAN, 15% Glass Fiber |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | |
| Ineos ABS NOVODUR® P3T ABS, Injection Grade
(discontinued **) Injection molding grade, higher heat resistance.Applications: Automotive industry.Information provided by the manufacturer.Novodur is produced by Styrolution (2014). This grade was discontinued pri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical XR404T ABS, Heat Resistance Feature: Injection Molding, Heat Resistance, Curl FitApplication: Automotives Interior Housing (P/W Switch Housing Etc)CAS No. 25120-20-1, 9003-56-9, and 9001-96-2Information provided by LG Chemical.. |
|||