- Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
- Samsung Cheil Industries Starex® GR-4020 ABS, 20% Glass Filled
Samsung Cheil Industries Starex® GR-4020 ABS, 20% Glass Filled
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® GR-4020 ABS, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 5.6 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.6 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength at Break | 93.2 MPa | 13500 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 88.3 MPa | 12800 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 5.30 GPa | 768 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 127 MPa | 18400 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 5.98 GPa | 868 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm @Thickness 6.35 mm |
1.29 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.735 J/cm @Thickness 3.17 mm |
1.38 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 6.40 mm |
221 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 107 °C | 225 °F | B/50; ISO R306 |
| 111 °C | 232 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 6.00 mm |
HB @Thickness 0.0591 - 0.236 in |
Users viewing this material also viewed the following:
- Ovation Polymers Nemcon™ H PK DP110/X5 Polyetheretherketone
- Asahi Kasei Tenac® LT805 Acetal Homopolymer, Low Friction Grade (discontinued **)
- DuPont Performance Polymers Zytel® EFE7374 BK416 Nylon 6 (Unverified Data**)
- HP Alloys Alloy C-276, 10% Cold Worked
- Taiwan PU Corporation TPU-BTB85 Breathable Grade, Blow Molding Polyether Base TPU
- ExxonMobil LDPE LD 123.LN Low Density Polyethylene Resin
- China Tungsten STG60Cu3Mo55 PM Structural Parts
- Abatron AboCast 8708-6 One-Component Structural/Dielectric Epoxy
- Overview of materials for Polyethylene Terephthalate (PET), 50% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved