Material Notes:
SABIC® PPcompound 7985 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with interior automotive UV stability. The IMDS is 209747565.
Physical Properties Metric English Comments
Specific Gravity 1.02 g/cc
1.02 g/cc
ASTM D792
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0080 cm/cm
0.0080 in/in
48 hrs @ 23°C, flow; SABIC Method
0.010 cm/cm
0.010 in/in
1 hr @ 80°C, flow; SABIC Method
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
48 hrs @ 23°C, xflow; SABIC Method
0.014 cm/cm
0.014 in/in
1 hr @ 80°C, xflow; SABIC Method
Melt Flow 21 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 21 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 66
66
ISO 868
Tensile Strength at Break 20.0 MPa
2900 psi
Type I, 50 mm/min; ASTM D638
20.0 MPa
2900 psi
50 mm/min, 1A; ISO 527
Tensile Strength, Yield 27.0 MPa
3920 psi
Type I, 50 mm/min; ASTM D638
27.0 MPa
3920 psi
50 mm/min; ISO 527
Elongation at Break 14 %
14 %
50 mm/min; ISO 527
22 %
22 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.19 GPa
318 ksi
1 mm/min; ISO 527
2.78 GPa
403 ksi
50 mm/min; ASTM D638
Flexural Modulus 1.94 GPa
281 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.22 GPa
322 ksi
2 mm/min, 64mm span; ISO 178
Izod Impact, Notched 0.450 J/cm
0.843 ft-lb/in
63.5*12.7*3.2mm, Cut; ASTM D256
Izod Impact, Unnotched 10.8 J/cm
20.2 ft-lb/in
63.5*12.7*3.2mm, Cut; ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4mm, Cut; ISO 180/1A
2.00 kJ/m²

@Temperature 0.000 °C
 0.952 ft-lb/in²

@Temperature 32.0 °F
 80*10*4mm, Cut; ISO 180/1A
2.00 kJ/m²

@Temperature -30.0 °C
 0.952 ft-lb/in²

@Temperature -22.0 °F
 80*10*4mm, Cut; ISO 180/1A
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
80*10*4mm, Cut; ISO 179/1eA
0.200 J/cm²

@Temperature 0.000 °C
 0.952 ft-lb/in²

@Temperature 32.0 °F
 80*10*4mm, Cut; ISO 179/1eA
0.200 J/cm²

@Temperature -30.0 °C
 0.952 ft-lb/in²

@Temperature -22.0 °F
 80*10*4mm, Cut; ISO 179/1eA
Dart Drop, Total Energy 2.00 J

@Temperature -30.0 °C
 1.48 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Energy @ peak, -30°C @ 6.6 m/s; ASTM D3763
7.00 J

@Temperature 0.000 °C
 5.16 ft-lb

@Temperature 32.0 °F
 Instrumented Impact Energy @ peak, @ 6.6 m/s; ASTM D3763
22.0 J

@Temperature 23.0 °C
 16.2 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 7.00 µm/m-°C

@Temperature -30.0 - 100 °C
 3.89 µin/in-°F

@Temperature -22.0 - 212 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 18.0 µm/m-°C

@Temperature -30.0 - 100 °C
 10.0 µin/in-°F

@Temperature -22.0 - 212 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 108 °C
226 °F
80*10*4mm, Cut; ISO 75-1&2
114 °C

@Thickness 3.20 mm
 237 °F

@Thickness 0.126 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 61.0 °C
142 °F
80*10*4mm, Cut; ISO 75-1&2
60.0 °C

@Thickness 3.20 mm
 140 °F

@Thickness 0.126 in
 ASTM D648
Vicat Softening Point 144 °C
291 °F
10N, 50°C/hr; ISO 306