Arkema Group Appryl® CZT 1030 Polypropylene, 30% Talc/Mica Filled

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler
Manufacturer Arkema
Trade Name Appryl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Appryl® CZT 1030 Polypropylene, 30% Talc/Mica Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Compound of a PP copolymer modified with EPR and 30% of a mixture of talc and mica. This grade has been specially developed for exterior automotive applications, that required an excellent thermal dimensional stability associated with a high modulus. It has a good paintability. Main application is rear and front panels.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 19.0 MPa
2760 psi
50 mm/min
Elongation at Break 7.0 %
7.0 %
Nominal Strain; 50 mm/min
Elongation at Yield 3.0 %
3.0 %
50 mm/min
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min
Charpy Impact Unnotched 4.60 J/cm²
21.9 ft-lb/in²
1.90 J/cm²

@Temperature -30.0 °C
9.04 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.10 J/cm²
5.24 ft-lb/in²
0.260 J/cm²

@Temperature -30.0 °C
1.24 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
Melting Point 163 °C
325 °F
10°C/min
Deflection Temperature at 0.46 MPa (66 psi) 108 °C
226 °F
Deflection Temperature at 1.8 MPa (264 psi) 64.0 °C
147 °F
Vicat Softening Point 52.0 °C
126 °F
50°C/hr; 50N