Inno-Comp INNOPOL® CS 2-9000 MA B Polypropylene Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Inno-Comp INNOPOL® CS 2-9000 MA B Polypropylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 2-9000 MA B is a black colored, high melt flow copolymer with antistatic additive.INNOPOL® CS 2-9000 MA B is developed for producing injection molded automotive components.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc <br>@Temperature 23.0 °C |
0.0325 lb/in³ <br>@Temperature 73.4 °F |
ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.022 cm/cm | 0.022 in/in | ISO 294 |
| Melt Flow | 36 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C |
36 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 25 % | 25 % | ISO 527-1,-2 |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.405 GPa | 203.8 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 1.55 GPa | 225 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 89.0 J/cm² <br>@Temperature -30.0 °C |
424 ft-lb/in² <br>@Temperature -22.0 °F |
PB; ISO 179/1eU |
| NB <br>@Temperature 23.0 °C |
NB <br>@Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.450 J/cm² <br>@Temperature -30.0 °C |
2.14 ft-lb/in² <br>@Temperature -22.0 °F |
ISO 179/1eA |
| 1.00 J/cm² <br>@Temperature 23.0 °C |
4.76 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | DSC; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ISO 75-1,-2 |
| Vicat Softening Point | 79.0 °C | 174 °F | B120; ISO 306 |
| 148 °C | 298 °F | A120; ISO 306 | |
| Flammability, UL94 | HB <br>@Thickness 1.60 mm |
HB <br>@Thickness 0.0630 in |
FMVSS 302 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive Materials | Pass | FMVSS 302 |
| Color | Black |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® ThinStik ShockSeal™ 79-09021 Self-Adhesive Urethane Foam
- Hybrid Plastics POSS® MA0704 MethacrylCyclohexyl-POSS®
- Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes
- Solvay Chemicals NOCOLOK® Thickener (water soluble)
- Stir SpA SR 75 REF (PVC)
- Master Bond EP21TDC-2 Highly Flexible Cryogenic Epoxy Compound
- Unifrax Fiberfrax® Fibermax® Caulk
- BASF Ultramid® C33 L PA6/66
- Beijing Ranger Chem SM-609R Solid Epoxy Resin
- Ravago Manufacturing Americas Echo® RPH20TC BK Recycled Polypropylene Homopolymer, 20% Talc Filled
Copyright © lookpolymers.com All Rights Reserved