- Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
- Samsung Cheil Industries Starex® GA-4025 ABS, 25% Glass Filled
Samsung Cheil Industries Starex® GA-4025 ABS, 25% Glass Filled
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® GA-4025 ABS, 25% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Permanent static prevention material with 25% GF reinforcement that can be used in OA device and trayInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 7.4 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.4 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Ash | 25 % | 25 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.6 MPa | 9950 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 68.6 MPa | 9960 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 2.1 % | 2.1 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 5.49 GPa | 797 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 88.3 MPa | 12800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 5.59 GPa | 811 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.402 J/cm @Thickness 6.35 mm |
0.753 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.471 J/cm @Thickness 3.17 mm |
0.882 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C @Thickness 6.40 mm |
216 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 104 °C | 219 °F | B/50; ISO R306 |
| 106 °C | 223 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 1.60 mm |
HB @Thickness 0.0591 - 0.0630 in |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Kemex™ V96E
- Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA) (Unverified Data**)
- SABIC Innovative Plastics PC1000 PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP JF004 PES (Europe-Africa-Middle East)
- Tipco Tipcolene® TPE-HMI TPE HMI - Impact Modified Polypropylene Copolymer Compound with High Flow, Soft Touch
- Eurostar Staramide AG4K PA66, 20% Glass Filled, Injection Molded
- Fainplast Compounds KL 0993 Flexible PVC, Insulation for High Temperatures Lead Free
- BCC Products Proto-Kast BC 8163 Urethane Casting
- 3M Scotch® 8898 Strapping Tape
- ATI Wah Chang Tiadyne™ 3510
Copyright © lookpolymers.com All Rights Reserved