Ascend Performance Materials VYDYNE® 45 Nylon, Impact Modified, Weather Stable
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Ascend Performance Materials (formerly Solutia) |
| Trade Name | VYDYNE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ascend Performance Materials VYDYNE® 45 Nylon, Impact Modified, Weather Stable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical property data. VYDYNE is a registered trademark of Solutia Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Water Absorption | 1.15 % | 1.15 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | ASTM D638 |
| Elongation at Break | 28 % | 28 % | ASTM D638 |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm @Thickness 3.17 mm |
2.25 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C @Thickness 3.20 mm |
172 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 3.20e+15 ohm-cm | 3.20e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.11 @Frequency 1e+6 Hz |
3.11 @Frequency 1e+6 Hz |
ASTM D150 |
| 3.47 @Frequency 1000 Hz |
3.47 @Frequency 1000 Hz |
ASTM D150 | |
| 3.56 @Frequency 100 Hz |
3.56 @Frequency 100 Hz |
ASTM D150 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | Step by step; ASTM D149 |
| 21.2 kV/mm | 538 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.020 @Frequency 100 Hz |
0.020 @Frequency 100 Hz |
ASTM D150 |
| 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
ASTM D150 | |
| 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- MV Labs IR440 H2IrCl6·xH2O Hydrogen hexachloroiridateIV) hydrate
- MV Labs MN400 MnCl2·4H2O Manganese(II) chloride tetrahydrate
- Parker Chomerics Tecknit NC-Consil® 750 Nickel Coated Graphite Filled Silicone Elastomer
- Plaskolite West Optix® CA-81 UVA-7 UV-Absorbing Acrylic Resin
- Michelman® Michem® Emulsion 27720 Nonionic slip and anti-block additive
- Styron EMERGEâ„¢ 5710 Acrylonitrile Butadiene Styrene (ABS)
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- Beijing Evergrow Resources Polyurethane Activated Carbon
- Dow Corning 3110 SILICONE RUBBER ENCAPSULANT
- DSM Novamid® 3021GH30 BK629 PA66-GF30
Copyright © lookpolymers.com All Rights Reserved