Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 103 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Cycolac® X37 ABS (Europe-Africa-Middle East) CYCOLAC X37 is the highest heat material available in the CYCOLAC range of materials and is widely recognized within the automotive industry as being the industry standard for high heat ABS. It comb..
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Cycoloy® C2950 PC+ABS (Europe-Africa-Middle East) Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C @Thickness 3.20 mm	217 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® C2951 PC+ABS (Asia Pacific) CYCOLOY C2951 is a flame retardant PC+ABS free from chlorinated or brominated flame retardant additives. High heat resistance is offered for demanding electrical applications, whilst maintaining exc..
Deflection Temperature at 0.46 MPa (66 psi)	103 °C @Thickness 3.20 mm	217 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics GELOY CR8510 ASA ASA with outstanding UV exposure performance for both exterior and interior applications. F1 Rated.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics GELOY CR8510 ASA (Asia Pacific) ASA with outstanding UV exposure performance for both exterior and interior applications. F1 Rated.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP FARADEX NX96302 PC+ABS LNP* FARADEX* NX96302 is a compound based on PC+ABS resin containing Stainless Steel Fibers.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F
Polimeri Europa KOBLEND PCA PD 55 PC+ABS (discontinued **) Symbol according to ISO 1043/1: PC+ABS Halogen free injection moulding grade with flame retardant properties ( UL 94 V-0 at 1.6mm thickness ). Main application fields: business machines, electroni..
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Unannealed; ASTM D648
Ravago Manufacturing Americas Hybrid B2035I Polycarbonate + PBT Alloy Available in North America High Impact Resistance Form: PelletsInformation provided by Ravago
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP BG004 SAN (Europe-Africa-Middle East) LNP* LUBRICOMP* BG004 is a compound based on Styrene Acrylonitril resin containing Graphite. Added features include: Internally Lubricated.
Deflection Temperature at 0.46 MPa (66 psi)	103 Â°C	217 Â°F	ISO 75-1,-2
Ineos ABS LustranÂ® SAN C Injection Molding Grade
Deflection Temperature at 0.46 MPa (66 psi)	103 Â°C	217 Â°F	ASTM D648
LG Chemical SEETEC H7511 Polypropylene, Homopolymer Features: Seetec H7511 is designed for the extrusion of staple fibers. This grade is characterized by high tenacity from narrow molecular weight distribution (MWD) and UV stability. SEETEC H7511 mee..
Deflection Temperature at 0.46 MPa (66 psi)	103 Â°C	217 Â°F	ISO 75-1,-2
Inno-Comp INNOPOLÂ® CS 2-2523 EP 16% Talc Filled, Elastomer Modified Polypropylene Copolymer INNOPOLÂ® CS 2-2523 EP is a 16% talc-filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in natural and custom colored form.INNOPOLÂ® CS 2-2523 EP..
Deflection Temperature at 0.46 MPa (66 psi)	103 Â°C	217 Â°F	ASTM D648-97
Ipiranga Petrochem PH 1721 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr..
Deflection Temperature at 0.46 MPa (66 psi)	103 Â°C	217 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP STAT-LOY AF306 ABS (Asia Pacific) LNP* Stat-loy* AF306 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. Added features of this material include: Antistat.
Deflection Temperature at 0.46 MPa (66 psi)	103 Â°C	217 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP AF004L ABS LNP* THERMOCOMP* AF004L is a compound based on ABS resin containing 20% Glass Fiber. Added feature of this material is: Low Extractible.
Deflection Temperature at 0.46 MPa (66 psi)	103 Â°C @Thickness 6.40 mm	217 Â°F @Thickness 0.252 in	ASTM D648
Samsung Cheil Industries InfinoÂ® EF-1032 PC/ABS, Unreinforced FR Extrusion resin, non-halogen flame-retardantInformation provided by Samsung Cheil Industries.
Deflection Temperature at 0.46 MPa (66 psi)	103 Â°C	217 Â°F	unannealed; ASTM D648
Styron Magnumâ„¢ 1250 BG Acrylonitrile Butadiene Styrene (ABS) High Impact, High Heat, Blow Molding ABSInformation provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	ISO 75
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	ASTM D648
Toyobo VYLOPET® EMC307 Injection Molding Polyester Resin, High Cycles Applications: Coiled bobbinsMouthpiecesFeatures: High cyclesInformation provided by Toyobo.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Unannealed; ASTM Data
Engineered Plastics EPABS 19 ABS Extrusion Grade Pellets. GMP # 002. Property values below represent typical values. Information provided by Engineered Plastics Corporation.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Flatw 80x10x4, sp=64 mm; ISO 75/Bf
Eurostar Starflam M10009AP PP, Flame Retardant, Injection Molding Starflam M10009AP is an Unfilled Flame Retardant high fluidity Polypropylene (Homo) Injection Molding ResinInformation provided by Eurostar.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Unannealed; ASTM Data
Engineered Plastics EPABS 54 ABS Injection Grade Pellets. GMP # 002. Property values below represent typical values. Information provided by Engineered Plastics Corporation.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	ASTM D648
Aclo Accutech Polypropylene Copolymer CP0437M20CL Mica Reinforced Coupled
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F
BASF Procom® D 1146 Polypropylene Data was collected by ISO methods and provided by BASF.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	ASTM D648
Ineos H20G-00 Polypropylene Homopolymer This is a general purpose homopolymer for injection molding applications. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsC..
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	ISO 75
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Xenoy® CL101D PBT+PC (Europe-Africa-Middle East) XENOY CL101D is an impact modified PBT+PC injection moulding resin with excellent low temperature impact performance. Applications: automotive exterior components such as bumper systems.This data wa..