SABIC Innovative Plastics LNP THERMOCOMP AF004L ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP AF004L ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* AF004L is a compound based on ABS resin containing 20% Glass Fiber. Added feature of this material is: Low Extractible.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.230 % | 0.230 % | 50% RH, 24 hrs; ASTM D570 |
| 0.280 % | 0.280 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.0 MPa | 10400 psi | 5 mm/min; ISO 527 |
| 77.0 MPa | 11200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| 2.1 % | 2.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 5.66 GPa | 821 ksi | 1 mm/min; ISO 527 |
| 5.94 GPa | 862 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 107 MPa | 15500 psi | ISO 178 |
| 109 MPa | 15800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 112 MPa | 16200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.92 GPa | 714 ksi | 2 mm/min; ISO 178 |
| 5.40 GPa | 783 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.820 J/cm | 1.54 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.64 J/cm | 6.82 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 49.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 66.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
36.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible R5160A Polyvinyl Chloride, Flexible (PVC, Flexible)
- Iran Petrochemical (PCC) 60505 High Density Polyethylene
- Möller Medical NanoSkin 90 NanoCoating
- Chase Plastics CP Pryme® NNA100 (Dry) ABS Polyamide Alloy
- A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
- Clariant Renol 6608G43 Nylon 66, 43% Glass Fiber, Impact Modified, Heat Stabilized, Lubricated
- Arkema Group Orgalloy® RS 6620 Nylon 66 Alloy, 20% Glass Fiber (Conditioned)
- BASF Basantol® 415 Bordeaux Liquid
- CeramTec 547 Cordierite (2MgO-2Al2O3-5SiO2)
- Buckeye Polymers BP Flex D4507 TPO
Copyright © lookpolymers.com All Rights Reserved