SABIC Innovative Plastics LNP FARADEX NX96302 PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP FARADEX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP FARADEX NX96302 PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* FARADEX* NX96302 is a compound based on PC+ABS resin containing Stainless Steel Fibers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| 0.170 % | 0.170 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | 5 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.1 % | 6.1 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 3.2 % | 3.2 % | 50 mm/min; ISO 527 |
| 3.7 % | 3.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.30 GPa | 479 ksi | 50 mm/min; ASTM D638 |
| 3.45 GPa | 500 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 109 MPa | 15800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.39 GPa | 492 ksi | 2 mm/min; ISO 178 |
| 3.59 GPa | 521 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.540 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.18 J/cm | 7.83 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 96.0 °C @Thickness 3.20 mm |
205 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 3.0 ohm | 1.0 - 3.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- LATI LAPEX A Polyethersulfone (PES) (UL94 V-0) (Unverified Data**)
- Solvay Specialty Polymers Halar® 558 Polyethylene, Chlorotrifluoroethylene (ECTFE) (Unverified Data**)<
- SABIC Innovative Plastics LNP THERMOCOMP PFB55 PA 6 (Europe-Africa-Middle East)
- Teknor Apex MONPRENE® MP 2840E Thermoplastic Elastomer
- PlastxWorld CEVIAN® S3100 PC/ABS alloy
- Hexcel® Redux® 101 Surface Pretreatment Protection Solution
- Cossa Polimeri ESTAPROP H 1080 TG Polypropylene, 40% Mineral Filled
- ELASTO UK Dryflex® 662900S SEBS Based Material, Semi-Filled Qualities, 90A Hardness, Black
- Dow 6D43 Polypropylene Random Copolymer Resin
- A. Schulman ComAlloy Lubrilon® 605 Nylon 6/6, PTFE Filled, Flow Enhanced
Copyright © lookpolymers.com All Rights Reserved