Toyobo VYLOPET® EMC307 Injection Molding Polyester Resin, High Cycles
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo VYLOPET® EMC307 Injection Molding Polyester Resin, High Cycles.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Coiled bobbinsMouthpiecesFeatures: High cyclesInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | MD |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength at Break | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 1.08 J/cm | 2.02 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 20 | 20 | CS-17; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 255 °C | 491 °F | By DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Thermal index; ASTM UL746B |
| 225 °C | 437 °F | Ball pressure temperature; IEC Method | |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.907 mm |
V-0 @Thickness 0.0357 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 125 sec | 125 sec | Tungsten electrode; ASTM D495 |
| Comparative Tracking Index | 250 - 399 V | 250 - 399 V | IEC Pub1.112, class 2; IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 255 - 265 °C | 491 - 509 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F |
Users viewing this material also viewed the following:
- MarkeTech Repton 504 Mullite
- Kingfa PA6-T25 25% Mineral Filled PA6
- SABIC Innovative Plastics LNP STAT-KON WEF32ISP PBT (Europe-Africa-Middle East)
- Saint-Gobain Chemfab® 11 Premium PTFE-Coated Glass
- ExxonMobil 763 Mobilmet 760 Series
- A. Schulman POLYTROPE™ TPP 512 Injection Molding Grade Olefinic Thermoplastic Elastomer
- ExxonMobil LDPE LD 152BW Low Density Polyethylene Resin
- Eurostar Staramide 6 70E3 PA6, 70% Mineral Filled, Injection Molded
- Eurostar Staramide AST43 PA66, Impact Modified, Injection Molded
Copyright © lookpolymers.com All Rights Reserved