Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 24.0 - 45.0 µm/m-°C @Temperature 50.0 - 100 °C |
13.3 - 25.0 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta.. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36E PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DFL36E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features include; Internally Lubricated, Easy Molding. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 20.0 °C |
13.3 µin/in-°F @Temperature 68.0 °F |
ISO data |
BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9333G is a 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface a.. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
Idemitsu Kosan Xarec® D132 SPS, 25% Glass Filled |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
Idemitsu Kosan Xarec® EA 522 SPS, 22% Glass Filled Crystalline Polymer, Glass Filled, Ignition Resistant, Impact Modified. Used in Electronic and Electrical applications |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
Idemitsu Kosan Xarec® N WA 7030 SPS, 30% Glass Filled Crystalline Polymer Blend, Glass Filled, Impact Modified |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 20.0 °C |
13.3 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Mitsui Arlen™ C230 30% Glass Fiber-Reinforced Modified Nylon 6T (COND) ARLEN™ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320°C) and a rigidity level comparable to super engineering plastics, it poss.. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
SABIC Innovative Plastics Valox® IQNH4560 PBT (Asia Pacific) Valox* IQNH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP THERMOCOMP HF006EU PA11 (Europe-Africa-Middle East) LNP* THERMOCOMP* HF006EU is a compound based on PA 11 resin containing Glass Fiber. Added features include: Easy Molding, UV-Stabilized. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP THERMOCOMP UF007SXC PPA (Europe-Africa-Middle East) LNP* THERMOCOMP* UF007SXC is a compound based on Polyphthalamide resin containing Glass Fiber. Added features include : Heat Stabilized . |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
SABIC Innovative Plastics LNP THERMOCOMP UF00ASW PPA LNP* Thermocomp* UF00ASW is a compound based on Polyphthalamide (PPA) containing glass fiber. Characteristics of this grade of Heat Stabilized and Hot Water Moldable. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 20.0 °C |
13.3 µin/in-°F @Temperature 68.0 °F |
ASTM E-831 |
Sumitomo Bakelite North America E 8398 Hardware Grade Epoxy Fiberglass and mineral reinforced epoxy molding compound with excellent dimensional stability, good electrical insulation properties, and good strength.Information provided by Vyncolit, a Sumitomo B.. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP STAT-KON RE007 PA 66 LNP* STAT-KON* RE007 is a compound based on PA66 resin containing 35% Carbon Fiber. Added features include: Electrically Conductive. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP THERMOCOMP 2FL24 ETFE LNP* THERMOCOMP* 2FL24 is a compound based on ETFE resin containing 20% Glass Fiber, 10% PTFE. Added feature of this grade is Wear Resistant. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
SABIC Innovative Plastics LNP Thermocomp 2FL24 FP-E (EFTE) LNP* 2FL24 is a Fluoropolymer, ETFE grade containing Glass Fibers and PTFE.This data was supplied by SABIC-IP for the Americas region. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 20.0 °C |
13.3 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
Sumitomo Bakelite North America FM 3001 Cellulose Reinforced Phenolic Novolac FM 3001 is a self-lubricated cellulose reinforced phenolic molding compound, modified for applications requiring reduced friction and low wear. Information supplied by Sumitomo Bak North America... |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP VERTON RV00AEXP PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AEXP is a compound based on PA 66 resin containing Long Glass Fiber. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP VERTON RV00ASXP PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00ASXP is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Heat Stabilized. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
Eurostar Staramide RF006EU PA66/6, Glass Fiber Filled, Injection Molded Staramide RF006EU is an UV stabilized, Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as Staramide 66C 30V S4)Information provided by Eurostar. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C | 13.3 µin/in-°F | ASTM Test |
BASF Petra® 130 FR 30% Glass Filled PET Petra 130 FR is a 30% glass fiber reinforced, flame retardant injection molding polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. It is also avail.. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C | 13.3 µin/in-°F | ISO 11359 |
BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Dry) Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a
balance of st.. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
13.3 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
Ascend Performance Materials Vydyne® R860 BK02 Nylon 66, Glass/Mineral Reinforced, DAM Vydyne® R860 BK02 is general-purpose, glass-fiber and mineral-reinforced PA66 resin. Available in black, this product is also lubricated for improved flow and offers superior surface appearance. Gl.. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 20.0 °C |
13.3 µin/in-°F @Temperature 68.0 °F |
ISO data |
BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G HI is a 33% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance .. |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP VERTON RV00ASXS PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00ASXS is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Heat Stabilized |
|||
CTE, linear, Parallel to Flow | 24.0 µm/m-°C | 13.3 µin/in-°F | ASTM D696 |
Kuraray Genestar™ G1300A-M41 Nylon, 30% Glass Filled Glass reinforced injection grade. Main Features:Chemical resistanceHeat resistanceExamples of applications:Gears and bearing retainersIntercooler tank and turbo duct pipe |