SABIC Innovative Plastics LNP THERMOCOMP UF00ASW PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UF00ASW PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* UF00ASW is a compound based on Polyphthalamide (PPA) containing glass fiber. Characteristics of this grade of Heat Stabilized and Hot Water Moldable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Density | 1.65 g/cc | 0.0596 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.270 % | 0.270 % | 50% RH, 24 hrs; ASTM D570 |
| 0.330 % | 0.330 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm @Time 86400 sec |
0.0060 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 214 MPa | 31000 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 214 MPa | 31000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 19.06 GPa | 2764 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 324 MPa | 47000 psi | ISO 178 |
| 337 MPa | 48900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 335 MPa | 48600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 17.24 GPa | 2500 ksi | 2 mm/min; ISO 178 |
| 17.5 GPa | 2540 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.88 J/cm | 14.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 296 °C | 565 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 297 °C @Thickness 3.20 mm |
567 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 281 °C | 538 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GBF 1010 35 BLACK 13 Polyamide 6 (Nylon 6)
- SABIC Innovative Plastics LNP LUBRICOMP 5CL24 PVDF
- Samsung Cheil Industries Infino® TN-1200 PC, Unreinforced FR
- Sinotek Materials ZSLG96 High Carbon Graphite
- ExxonMobil Mobil 1 20W-50 Motorcycle Oil V-Twin 4-Cycle
- Wellman Wellamid® GFX1743-N1(PTFE) 45% Glass Fiber Reinforced, Enhanced Lubrication Nylon 66/6
- Zeon Chemicals Nipol® 1082V Polyblend Nitrile Elastomer
- Arlon Thermabond® R37623X008 0.0050" Cured Silicone Rubber with Fiberglass Substrate
- Advanced Elastomer Systems Santoprene® 283-40 Thermoplastic Rubber (discontinued **)
- ExxonMobil Escorene™ LD 705.MJ Blown Ethylene Vinyl Acetate Copolymer
Copyright © lookpolymers.com All Rights Reserved