Eurostar Staramide RF006EU PA66/6, Glass Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/Nylon 6 Blend, Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide RF006EU PA66/6, Glass Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide RF006EU is an UV stabilized, Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as Staramide 66C 30V S4)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 3.0 % @Temperature 23.0 °C, Time 86400 sec |
3.0 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 4.00 mm |
0.0020 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 170 MPa | 24700 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.3 % | 3.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.80 GPa | 1280 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 233 MPa | 33800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80x10x4; ISO 179/1eA |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² | 38.1 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 255 - 275 °C | 491 - 527 °F | |
| Zone 2 | 265 - 275 °C | 509 - 527 °F | |
| Zone 3 | 265 - 275 °C | 509 - 527 °F | |
| Melt Temperature | 265 - 275 °C | 509 - 527 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Ryton® R-4XT Polyphenylene Sulfide Compound (Unverified Data**)
- LTL Color Compounds ColorFast® PCT2010 PC/PCT Alloy, Chemical Resistant
- Haysite H515 Polyester, High Temp Flex
- SABIC Innovative Plastics NORYL FXN4020H PPE+HIPS (Asia Pacific)
- Dow LDPE 682I Low Density Polyethylene, Film Grade
- Arlon 920-10Hxx-P0 0.020" Self-Fusing Silicone Rubber Tape
- 3M Scotchkote™ 162CR Epoxy Coating
- Eurotec® Tecomid® NB40 KG30NL IX PA6, 30% glass fiber/glass bead reinforced, impact modified, natural
- SABIC Innovative Plastics LNP VERTON RX00078 PA 66 (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved