- Idemitsu Kosan Xarec® D132 SPS, 25% Glass Filled
Idemitsu Kosan Xarec® D132 SPS, 25% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® D132 SPS, 25% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | |
| 1.24 g/cc | 0.0448 lb/in³ | ||
| Filler Content | 25 % | 25 % | |
| 25 % | 25 % | ||
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH |
| 0.010 % | 0.010 % | 24 hrs., 50% RH | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |
| 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | |
| 125 MPa | 18100 psi | ||
| Elongation at Break | 2.3 % | 2.3 % | |
| 2.3 % | 2.3 % | ||
| Tensile Modulus | 8.20 GPa | 1190 ksi | |
| 8.20 GPa | 1190 ksi | ||
| Flexural Yield Strength | 195 MPa | 28300 psi | |
| 195 MPa | 28300 psi | ||
| Flexural Modulus | 7.80 GPa | 1130 ksi | |
| 7.80 GPa | 1130 ksi | ||
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | |
| 13.0 kJ/m² | 6.19 ft-lb/in² | ||
| Izod Impact, Unnotched (ISO) | 43.0 kJ/m² | 20.5 ft-lb/in² | |
| Charpy Impact Unnotched | 4.70 J/cm² | 22.4 ft-lb/in² | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
| CTE, linear, Transverse to Flow | 39.0 µm/m-°C | 21.7 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comments | NSF61 | |
| SPS blend optimized for ductility & fatigue resistance |
Users viewing this material also viewed the following:
- Polyplastic Armlen® PP MF 20-3IM Impact Modified Polypropylene
- NanoScale NanoActive® Aluminum Oxide Plus
- Saint-Gobain CHR® SG15-14(R) High Performance Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Sichuan Deyang Haton® hGR505 Polyphenylene Sulfide/PA Alloy
- SABIC Innovative Plastics LNP THERMOCOMP OF008E PPS (Asia Pacific)
- Saint-Gobain Norton® Fluorglas® Chemfilm® R128/R129 Premium Grade Extruded Full Density PTFE Film (0.003" thick)
- Saint-Gobain Chemfab® 14 Porous PTFE-Coated Glass
- Hexcel® HexForce™ AGP370-5H Carbon Fabric
- 3M Jet-Weld™ TE-015 Adhesive
Copyright © lookpolymers.com All Rights Reserved