Kuraray Genestar™ G1300A-M41 Nylon, 30% Glass Filled

Category	Polymer , Thermoplastic , Nylon
Manufacturer	Kuraray Company
Trade Name	Genestar™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Kuraray Genestar™ G1300A-M41 Nylon, 30% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Glass reinforced injection grade. Main Features:Chemical resistanceHeat resistanceExamples of applications:Gears and bearing retainersIntercooler tank and turbo duct pipe

Physical Properties	Metric	English	Comments
Specific Gravity	1.37 g/cc	1.37 g/cc
Density	1.37 g/cc	0.0495 lb/in³	ISO 1183
Water Absorption	0.19 %	0.19 %	ISO 62
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	190 MPa	27600 psi	ISO 527-1/-2
Elongation at Break	2.5 %	2.5 %	ISO 527-1/-2
Tensile Modulus	9.74 GPa	1410 ksi	ISO 527-1/-2
Flexural Strength	270 MPa	39200 psi	ISO 178
Flexural Modulus	8.80 GPa	1280 ksi	ISO 178
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	ISO 179/1eA
Coefficient of Friction	0.40	0.40	ISO JIS K7218-A
K Factor (Wear Factor)	40	40	[mg]
Limiting Pressure Velocity	1.00 MPa-m/sec	28600 psi-ft/min

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	24.0 µm/m-°C	13.3 µin/in-°F	ASTM D696
CTE, linear, Transverse to Flow	41.0 µm/m-°C	22.8 µin/in-°F	ASTM D696
Melting Point	300 °C	572 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	270 °C	518 °F	ISO 75-1/-2
Glass Transition Temp, Tg	125 °C	257 °F	10°C/min; ISO 11357-1/-2

Descriptive Properties	Value	Comments
Additives	Release Agent
Applications	Automotive
	General Purpose
Chemical Resistance	Acid Resistance
	Alkali Resistance
	Environmental Stress Crack Resistance
	General Chemical Resistance
	Grease Resistance
	Hydrolytically Stable
	Oil Resistance
	Solvent Resistance
Delivery Form	Black
	Natural Color
Other Features	Barrier Properties
	Creep Resistance
	High Crystalinity
	Thermal Stability
	Weldable
Regional Availability	Asia Pacific
	Europe
	Near East/Africa
	North America
	South and Central America
Special Characteristics	Heat Stabilized or Stable to Heat

Users viewing this material also viewed the following: