BASF Petra® 130 FR 30% Glass Filled PET

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant
Manufacturer BASF
Trade Name Petra®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Petra® 130 FR 30% Glass Filled PET.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Petra 130 FR is a 30% glass fiber reinforced, flame retardant injection molding polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. It is also available in pigmented versions.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ISO 1183
Viscosity Measurement 0.49
0.49
Inherent Viscosity
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM Test
Tensile Strength at Break 130 MPa
18900 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 130 MPa
18900 psi
5mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5mm/min; ISO 527
2.0 %
2.0 %
0.2 in/min; ASTM Test
Tensile Modulus 11.1 GPa
1610 ksi
1mm/min; ISO 527
Flexural Strength 210 MPa
30500 psi
ASTM Test
85.0 MPa

@Temperature 120 °C
12300 psi

@Temperature 248 °F
ASTM Test
275 MPa

@Temperature -40.0 °C
39900 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 9.70 GPa
1410 ksi
ASTM Test
2.97 GPa

@Temperature 120 °C
431 ksi

@Temperature 248 °F
ASTM Test
Izod Impact, Notched 0.900 J/cm

@Thickness 3.17 mm
1.69 ft-lb/in

@Thickness 0.125 in
ASTM Test
Thermal Properties Metric English Comments
CTE, linear 24.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
13.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 24.0 µm/m-°C
13.3 µin/in-°F
ASTM Test
Melting Point 245 °C
473 °F
10 K/min
245 °C
473 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 240 °C
464 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75
220 °C
428 °F
ASTM Test
Flammability, UL94 V-0

@Thickness 0.300 mm
V-0

@Thickness 0.0118 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
5VA

@Thickness 0.800 mm
5VA

@Thickness 0.0315 in
Oxygen Index 36 %
36 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
IEC 60250
3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
IEC 60250
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 60243-1
Dissipation Factor 0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
0.020

@Frequency 100 Hz
0.020

@Frequency 100 Hz
IEC 60250
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 115 °C
239 °F
Injection molding
Injection Velocity 115 mm/sec
4.53 in/sec
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Flame retarding agent
UL.UL-C Yes