A. Schulman ComAlloy Hiloy® 121 Polypropylene, Glass Reinforced, Chemically Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 121 Polypropylene, Glass Reinforced, Chemically Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.11% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 89 | 89 | ASTM D785 |
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 8.3 % | 8.3 % | ASTM D638 |
| Flexural Strength | 56.0 MPa | 8120 psi | ASTM D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.02 J/cm | 9.40 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 229 - 246 °C | 444 - 475 °F |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1200-50VE 1200-50 VE SMC (discontinued **)
- KYDEX® 110 Metallic Thermoplastic Fire-rated Sheet
- H.C. Starck Amperweld® 1701.39 K4 Chromium Carbide RIII
- Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C
- A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene
- 3A Composites Core Materials AIREX® PXw.385 Fiber-Reinforced Structural Foam Panel
- Quadrant EPP Semitron® ESd 225, Extruded, Static Dissipative Acetal (ASTM Product Data Sheet)
Copyright © lookpolymers.com All Rights Reserved