Inno-Comp INNOPOL® CS 2-7120 20% Talc Filled Polypropylene Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 2-7120 20% Talc Filled Polypropylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 2-7120 is a 20 % talc-filled polypropylene block-copolymer compound /PP-B TD20 (ISO 1043)/. This grade is available in natural and custom colored form.INNOPOL® CS 2-7120 is recommended for extrusion of sheets and profiles, where the required properties are the balanced stiffness and impact resistance.Information provided by INNO-COMP
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Melt Flow | 0.80 g/10 min @Load 5.00 kg, Temperature 230 °C |
0.80 g/10 min @Load 11.0 lb, Temperature 446 °F |
nozzle diam 2.095 mm; ISO 1133 |
| Storage Temperature | <= 60.0 °C | <= 140 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 24.0 MPa | 3480 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Extrusion |
| Middle Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Extrusion |
| Front Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Extrusion |
| Die Temperature | 190 - 220 °C | 374 - 428 °F | Extrusion |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Extrusion |
| Moisture Content | <= 0.070 % | <= 0.070 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Designation | PP-B TD20 | ISO 1043 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF30 - PP Homopolymer Polypropylene, 30% Long Glass Fiber Reinforced
- Network Polymers NPP 50-0252
- Quadrant EPP Nylatron® LFG PA 6 + oil, cast (ISO Data)
- DuPont Performance Polymers Zytel® 157HSL BK010 Nylon 612 (Unverified Data**)
- SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK
- PlastxWorld CEVIAN®-N 050 SAN resin
- A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT
- Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, TVR380/26% Fiber
- Atom Adhesives AA-BOND F131 Epoxy Adhesive
- A. Schulman CP812 Linear, Medium-Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved