- Lehmann & Voss LUVOCOM® 50-7216 Polycarbonate, with PTFE, easy flowing
Lehmann & Voss LUVOCOM® 50-7216 Polycarbonate, with PTFE, easy flowing
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50-7216 Polycarbonate, with PTFE, easy flowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Impact resistance.Body and duty parts in office equipment, gear wheels, grippers, sleeves, sliding elements, switches and plugs.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 50.0 MPa | 7250 psi | |
| Elongation at Yield | 4.5 % | 4.5 % | |
| 5.5 % | 5.5 % | flexural | |
| Modulus of Elasticity | 2.30 GPa | 334 ksi | |
| Flexural Strength | 80.0 MPa | 11600 psi | |
| Flexural Modulus | 1.80 GPa | 261 ksi | |
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | flatwise; ISO 179 1fU |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term | |
| Vicat Softening Point | 160 °C | 320 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® PE 1296 Conductive Thermoplastic Compound
- PTS Trimid® N66-S100L High Impact Nylon 6/6
- SABIC Innovative Plastics LNP STAT-LOY KX05015 Acetal Copolymer (Europe-Africa-Middle East)
- A. Schulman PP 1500X-01 Polypropylene High Impact Copolymer Polypropylene
- ExxonMobil 120 Exxon Aviation Oil EE Series
- EMS-Grivory Grivory® L 20A Z PA12
- Covestro Bayblend® KU 1-1446* Polycarbonate + ABS
- Azoty Tarnow™ Tarnamid® T-27 GF50 Polyamide 6 - Glass Fiber Reinforced
- Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 10% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved