- LyondellBasell Hostacomâ„¢ XFBR712 Thermoplastic Polyolefin Elastomer
LyondellBasell Hostacomâ„¢ XFBR712 Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hostacom™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hostacomâ„¢ XFBR712 Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hostacomâ„¢ XFBR712 medium melt flow, 1,800 MPa flexural modulus, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of stiffness, impact resistance and dimensional stability. It was designed primarily for painted automotive interior components. Uses: Automotive interior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 49 | 49 | ISO 2039-2 |
| Hardness, Shore D | 58 | 58 | ISO 868 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527-1, -2 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1, -2 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 16.0 kJ/m² @Temperature 10.0 °C |
7.61 ft-lb/in² @Temperature 50.0 °F |
ISO 180 | |
| 34.0 kJ/m² @Temperature 23.0 °C |
16.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 48.0 µm/m-°C @Temperature -30.0 - 100 °C |
26.7 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 0.70 % | 0.70 % | Tool, 100x150x3.2 mm, injection molded plaque; Basell Test Method |
| 0.900 % @Temperature 121 °C, Time 3600 sec |
0.900 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Resin Technology Group 370 Wire Tacking Fusion™ Cyanoacrylate Instant Ethyl Adhesive
- MV Labs TL700 TlNO3 Thallium(I) nitrate
- SABIC Innovative Plastics LNP LUBRICOMP DFL36 PC (Europe-Africa-Middle East)
- A. Schulman POLYBLAK™ 4479-01A Black Color Concentrate, 50% Carbon Black Based In Polyethylene
- CP-Polymer-Technik Wellamid® 6600/50 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Dry
- Dow Elite® 5400 Linear Low Density Polyethylene
- Eurostar Staramide BG10 PA6, 50% Glass Filled, Injection Molded
- Momentive Performance Materials HV 3/706 Heat Cured Rubber - High Temperature
- Glastic GLASGUARD Scuff and Bulkhead Liners
Copyright © lookpolymers.com All Rights Reserved