Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
NYCOA 5033 HST 33% Glass-Fiber Reinforced, Heat Stabilized, Translucent Nylon 66 Resin NYCOA 5033 HST is a 33% glass fiber reinforced, heat stabilized, translucent Nylon 66 resin used for injection molding. It has been specifically formulated for see through storage tanks for automoti.. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | |
Plastcom SLOVAMID 6 GF 25 FRG 5 PA6, 25% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 25% glass fibre, with nonhalogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6 mm, glow wire at 960°.. |
|||
Flexural Modulus | 8.91 GPa | 1290 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36EU PC LNP* Lubricomp* DFL36EU is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated, Easy Molding and UV Stabilized. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | d.a.m., 2 mm/min; ISO 178-A |
Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS. |
|||
Flexural Modulus | 8.87 GPa | 1290 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP IFP36 PA6.12 LNP* LUBRICOMP* IFP36 is a Nylon 6/12 base resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of t his grade include: Wear Resistant. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | 2 mm/min, 64mm span; ISO 178 |
SABIC Innovative Plastics SABIC PPCOMPOUND G3240A PP SABIC® PPcompound G3240A is a general purpose, 40% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS ID is 139448304. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | 2 mm/min, 64mm span; ISO 178 |
SABIC Innovative Plastics SABIC PPCOMPOUND G3240U PP SABIC® PPcompound G3240U is a general purpose, 40% glass filled, chemically coupled, heat stabilized and UV stabilized homopolymer polypropylene compound. The IMDS ID is 209768078. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret.. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT (Asia Pacific) LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret.. |
|||
Flexural Modulus | 8.91 GPa | 1290 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® IQ507 PBT+PC Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characte.. |
|||
Flexural Modulus | 8.89 GPa | 1290 ksi | ASTM D790 |
Techmer ES HiFill® PA6/6 GF33 HR HS BK 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Heat StabilizerFeatures: Heat Stabilized and Hydrolysis Resistant Appearance: .. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP GF006 PSU (Europe-Africa-Middle East) LNP* THERMOCOMP* GF006 is a compound based on Polysulfone resin containing Glass Fiber. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 (Asia Pacific) LNP* Thermocomp* QF007 is a compound based on Nylon 6/10 resin containing Glass Fiber. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF006EXZ PA 66 LNP THERMOCOMP* RF006EXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF006 is a compound based on PPE+PS Blend resin containing Glass Fiber. |
|||
Flexural Modulus | 8.91 GPa | 1290 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Verton NV0061EV_GY7E148 PC+ABS Preliminary data for 30% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 8.91 GPa | 1290 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp XF006S LNP* Thermocomp* XF006S is a compound based on Amorphous Nylon containing Glass Fiber. Characteristics of this grade are: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.. |
|||
Flexural Modulus | 8.91 GPa | 1290 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP XF006S PA LNP* THERMOCOMP* XF006S is a compound based on Amorphous Nylon containing 30% Glass Fiber. Added feature of th is grade is: Heat Stabilized. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
Zhejiang Double Fish YS-G050 50% Long Fiber Glass Reinforced Polypropylene Features high strength, good surface quality, and easy processing. Typical applications include automobile (bumper back beam, arm rest core, instrument panel, mudflap), machinery, electronics, comm.. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
Toyobo VYLOPET® EMC317A Injection Molding Polyester Resin, Warpageless Applications: Iron's heat insulation plateChair framesHousingsFeatures: WarpagelessInformation provided by Toyobo. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
Plenco 4504 Phenolic, Granular, Injection Molded Plenco 04504 is a renumber of Plaslok 504. Plenco 04504 is a two-stage, mineral and cellulose-filled phenolic molding compound having better impact and heat resistance than general purpose molding c.. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790, ISO 178 |
EPICHEM Epinyl PA 66 GF 30 Polyamide 66, 30% Glass Characteristics: 30% glass fibre filled |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | 2 mm/min; ISO 178 |
Eurostar Starflam AFR450B PA66, 25% Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR450B is a Flame Retardant, 25% Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | 2 mm/min; ISO 178 |
Eurostar Starflam AFR450B1 PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR450B1 is a Flame Retardant, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
BLUESTAR 203G30 PBT, 30% Glass Filled Typical Applications: Thinner wall partsInformation provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
Solvay TECHNYL® 1021GF6 PA6, 30% glass fiber, DRY Description: Polyamide 6, 30% glass fiber reinforced, for injection molding.Available in: Asia Pacific Product Applications: TECHNYL® 1021GF6 is used in all sectors of industry, offering an excelle.. |
|||
Flexural Modulus | 8.91 GPa | 1290 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP JF006EXZ PES LNP* THERMOCOMP* JF006EXZ is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding. |