SABIC Innovative Plastics SABIC PPCOMPOUND G3240U PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND G3240U PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound G3240U is a general purpose, 40% glass filled, chemically coupled, heat stabilized and UV stabilized homopolymer polypropylene compound. The IMDS ID is 209768078.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | 48 hrs @ 23°C, flow; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | 48 hrs @ 23°C, xflow; SABIC Method |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | 50 mm/min, 1A; ISO 527 |
| 120 MPa | 17400 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 50 mm/min; ASTM D638 |
| 2.9 % | 2.9 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 7.61 GPa | 1100 ksi | 50 mm/min; ASTM D638 |
| 8.90 GPa | 1290 ksi | 1 mm/min; ISO 527 | |
| Flexural Modulus | 7.80 GPa | 1130 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.90 GPa | 1290 ksi | 2 mm/min, 64mm span; ISO 178 | |
| Izod Impact, Notched | 0.970 J/cm | 1.82 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D256 |
| Izod Impact, Unnotched | 6.10 J/cm | 11.4 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Gardner Impact | 0.300 J | 0.221 ft-lb | ASTM D5420 |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C @Temperature -30.0 - 100 °C |
8.89 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 155 µm/m-°C @Temperature -30.0 - 100 °C |
86.1 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C | 322 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 153 °C | 307 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 153 °C @Thickness 3.20 mm |
307 °F @Thickness 0.126 in |
ASTM D648 | |
| Vicat Softening Point | 164 °C | 327 °F | 10N, 50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- Qualchem Danamid FE Polyamide 6
- NOVA Chemicals Novapol® TF-0219-E Hexene LLDPE Film Resin
- LyondellBasell Alathon® M6080WC High Density Polyethylene
- Momentive Performance Materials Siloprenâ„¢ LSR 4640 FC Liquid Silicone Rubber - Healthcare
- SABIC Innovative Plastics ULTEM CRS5201R PEI (Asia Pacific)
- SABIC Innovative Plastics LNP VERTON MV006S PP (Europe-Africa-Middle East)
- Trelleborg R503 Commercial Natural Rubber Polyisoprene
- BASF 2-Ethylhexyl Choroformate
- Plenco 7579 Phenolic, Granular, Compression Molded
- DuPont Fusabond® MB528D Linear Low Density Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved